Abstract:Chemical anchor effect is an efficient route for polysulfides immobilization to enhance the performance of Li-S battery. Transition metal oxides are suitable chemical anchor matrix as Lewis acid coordinated with sulfur atoms in the form of Lewis base. Ion bonds may also be formed between anions in transition metal compounds and lithium ions in lithium polysulfides alleviating the shuttle effect. Reducing their crystal sizes to expose more surface active sites and expand surface areas is pivotal to sufficiently immobilize polysulfides. Here, an optimized GFM-2 composite was fabricated, where the 20 nm metal oxide particles aggregated by the 3-5 nm Fe2O3 and Mn3O4 binary crystals are uniformly distributed on the reduced graphene oxide (rGO) nanosheets. A high specific surface area up to 144.9 m(2) g(-1) was obtained for the GFM-2. The modified sulfur@rGO (S@G) cathode obtained by mixing S@G and GFM-2 additive with the mass ratio of 20: 1, presented high specific discharge capacities of 1356.3 and 770.2 mAh g(-1) , respectively, at scan rates of 0.1 and 5C (1C = 1675 mAh g(-1)) under conventional electrolyte dosage with electrolyte/sulfur (E/S) = 30 mL g((s))(-1). and sulfur loading of 1.1 mg cm(-2). The capacity was 1053.5 mAh g(-1) at 1C and maintained at 530.1 mAh g(-1) after 1000 cycles with the low average capacity decay rate of each cycle of 0.049%. Under low electrolyte dosages of E/S = 15 and 8 mL g((s))(-1) the high capacities of 1308.0 and 1230.4 mAh g(-1) could be still obtained at 0.1C, respectively. When the sulfur loading was increased to 2.8 mg cm(-2) and E/S was reduced to 10 mL g((s))(-1), the good capacity of 1163.6 mAh g(-1) was gotten at 0.1C. The high capacity and high cyclic property under different E/S and sulfur loading amounts indicate the potential for practical application of this simple but effective modified sulfur cathode. (C) 2020 Elsevier Ltd. All rights reserved.

Understanding the high-performance Fe(OH)3@GO nanoarchitecture as effective sulfur hosts for the high capacity of lithium-sulfur batteries

Understanding the high-performance Fe(OH)<sub>3</sub>@GO nanoarchitecture as effective sulfur hosts for the high capacity of lithium-sulfur batteries

3D Net-like GO-d-Ti3C2Tx MXene Aerogels with Catalysis/Adsorption Dual Effects for High-Performance Lithium-Sulfur Batteries

Hierarchical High‐Porosity Graphene Oxide‐Porous Carbon/Sulfur Composite with Sodium Chloride As Temporary Space Holders for High‐Performance Lithium‐Sulfur Batteries

Rational design of Ni3(HITP)2@GO composite for lithium-sulfur cathode

Construction of S@TiO2@r‐GO Composites for High‐Performance Lithium–Sulfur Batteries

3D S@MoS2@reduced graphene oxide aerogels cathode for high-rate lithium-sulfur batteries

Co9S8 nanotube wrapped with graphene oxide as sulfur hosts with ultra-high sulfur content for lithium-sulfur battery

A Rgo-Based Fe2O3 and Mn3O4 Binary Crystals Nanocomposite Additive for High Performance Li–S Battery

High-rate lithium-sulfur batteries enabled via vanadium nitride nanoparticle/3D porous graphene through regulating the polysulfides transformation

High‐Entropy Spinel Oxide Nanofibers as Catalytic Sulfur Hosts Promise the High Gravimetric and Volumetric Capacities for Lithium–Sulfur Batteries

Covalent organic framework wrapped by graphene oxide as an efficient sulfur host for high performance lithium–sulfur batteries

Porous honeycomb-like C3N4/rGO composite as host for high performance Li-S batteries

A MnO2/Graphene Oxide/Multi-Walled Carbon Nanotubes-Sulfur Composite with Dual-Efficient Polysulfide Adsorption for Improving Lithium-Sulfur Batteries

Sandwich-like NOCC@S8/rGO composite as cathode for high energy lithium-sulfur batteries

Rational Design of Graphene Oxide Wrapped Porous Microspheres As High-Performance Sulfur Cathode in Lithium-Sulfur Batteries

Loading Fe3O4 nanoparticles on N, S co-doped graphene suppressing polysulfides conversion toward high-performance Li–S batteries

A MnO 2 /Graphene Oxide/Multi-Walled Carbon Nanotubes-Sulfur Composite with Dual-Efficient Polysulfide Adsorption for Improving Lithium-Sulfur Batteries.

Porous Three-Dimensional Reduced Graphene Oxide for High-Performance Lithium-Sulfur Batteries

Three-dimensional embroidered ball-like alpha-Fe2O3 synthesised by a microwave hydrothermal method as a sulfur immobilizer for high-performance Li-S batteries

In situ conversion to construct fast ion transport and high catalytic cathode for high-sulfur loading with lean electrolyte lithium–sulfur battery