Abstract:Laser powder bed fusion (LPBF) additive manufacturing of zinc (Zn) offers promising advantages for biodegradable metal bone implants, including tailorable microstructures, controllable porous structures, and appropriate degradation rates. However, the layer-by-layer construction during LPBF often leads to microstructural and performance anisotropy within metallic materials. In this work, the anisotropic mechanical and degradation properties of pure Zn processed using LPBF were comprehensively investigated for the first time. Specifically, the influence of microstructural characteristics on the mechanical and degradation properties of LPBF-processed Zn in both horizontal and vertical planes was revealed, while the underlying deformation mechanisms in different planes were illustrated. The results demonstrated that the horizontal plane exhibited higher mechanical strength compared to the vertical plane, with ultimate tensile strength of 123.6 and 107.86 MPa, respectively, significantly surpassing that of the traditionally cast counterpart (52.7 MPa). Importantly, abundant deformation twins coupled with infrequent microbands and pyramidal ( c + a ) slip systems activated during tensile loading along the vertical plane enabled multiple deformation modes, which sustained durable work hardening ability while delaying plastic instability, resulting in extraordinary plasticity (elongation of 14.2 %). Additionally, synergistic effects between high-density grain boundaries including low-angle grain boundaries and pre-existing dislocations promoted the stable presence of a passive film along the horizontal plane, thus exhibiting relatively low corrosion sensitivity. Furthermore, the LPBF-processed Zn also demonstrated favorable biological activity and osteogenic potential. These findings provide valuable insights into multiple mechanisms underlying anisotropy in mechanical and degradation properties of laser additively manufactured Zn-based materials. (c) 2024 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.

Tunable zinc corrosion rate by laser surface modification for implants with controllable degradation direction

Surface Modification on Biodegradable Zinc Alloys

Effect of surface modification by nanosecond laser texturing on pure Zn biodegradability

Revealing Anisotropic Mechanisms in Mechanical and Degradation Properties of Zinc Fabricated by Laser Powder Bed Fusion Additive Manufacturing

Revealing Anisotropic Mechanisms in Mechanical and Degradation Properties of Zinc Fabricated by Laser Powder B E D Fusion Additive Manufacturing

The effect of topological design on the degradation behavior of additively manufactured porous zinc alloy

Enhancing control over the degradation behavior of zinc alloy via MOF coating

Recent progress and perspectives in laser additive manufacturing of biodegradable zinc alloy

Laser Additive Manufacturing of Zinc Targeting for Biomedical Application

Surface Modification of Biodegradable Zinc Alloy for Biomedical Applications

Study on the Enhanced Degradable Rate of the Zn-0.4Li Alloys as Biodegradable Implants by Anodization

Laser additive manufacturing of zinc: formation quality, texture, and cell behavior

Microstructural Evolution, Mechanical Properties and Corrosion Mechanisms of Additively Manufactured Biodegradable Zn-Cu Alloys

Surface Modification of Pure Zinc by Acid Etching: Accelerating the Corrosion Rate and Enhancing Biocompatibility and Antibacterial Characteristics

Fabrication and performance of Zinc-based biodegradable metals: From conventional processes to laser powder bed fusion

Enhancing wear resistance and biocompatibility of medical ZrNb alloy used for artificial joint via femtosecond laser surface processing combined with thermal oxidation

Laser additive manufacturing of Zn metal parts for biodegradable applications: Processing, formation quality and mechanical properties

Effect of building orientation on the in vitro corrosion of biomedical Zn-Cu alloys prepared by selective laser melting

Design of magnesium alloys with controllable degradation for biomedical implants: From bulk to surface

Laser-Guided Corrosion Control: A New Approach to Tailor the Degradation of Mg-Alloys.

Tunability of mechanical and biodegradation properties of zinc-based biomaterial with calcium Micronutrient alloying