Effect of Cr on the Microstructure and Strength‐Toughness of High‐Strength and Heat‐Resistant Stainless Steel
Hongxiao Chi,Liping Pian,Jinbo Gu,Yong Sun,Xuedong Pang,Zhenfei Xin,Dangshen Ma
DOI: https://doi.org/10.1002/srin.202400412
IF: 2.1258
2024-09-02
steel research international
Abstract:The strength‐toughness and microstructure evolution of high‐strength and heat‐resistant stainless steel with different Cr contents (8, 10, and 13.5%) are investigated by tensile and fracture toughness test. The increase of Cr content enhances the toughness and decreases the lattice misfit between ferric matrix and M2C precipitates, reducing the coherency strengthening. The effect of Cr content on the microstructure and mechanical properties of CSS‐42L steel is investigated by X‐ray diffractometer, scanning electron microscopy, and transmission electron microscopy. The results show that increasing Cr from 8% to 13.5% significantly improves toughness and ductility while moderately decreasing the strength. The tensile strength, fracture toughness (KIC), and impact absorbing energy of 13.5% Cr steel are 1.8 GPa, 88.6 MPa√m, and 58.5 J, respectively. 13.5%Cr steel possesses larger grain size and fewer undissolved M6C carbides than 8%Cr and10%Cr steels, which is attributed to that Cr addition increases Cr content in the (Mo,Cr)6C, reducing the dissolution temperature and ability to inhibit grain growth. Cr significantly decreases the Martensite start (Ms) temperature from 263 to 53.1 °C and increases the retained austenite from 0.3 to 13.19 vol%. Cr increases the number density and diameter of nanoscale M2C, which is attributed to Cr promoting the dissolution of Mo and increasing the nucleation rate. Meanwhile, the higher Cr content also increases the growth rate of the carbides along the diameter direction. Cr addition reduces the contribution from coherency strengthening caused by decreased lattice misfit and increased the contribution of Orowan dislocation looping resulted from higher volume fraction and size of M2C.
metallurgy & metallurgical engineering