Synthesis and Characterizations of Branched Poly(butylene Succinate) Copolymers with 1,2‐octanediol Segments
Guoli Wang,Bing Gao,Haimu Ye,Jun Xu,Baohua Guo
DOI: https://doi.org/10.1002/app.32168
IF: 3
2010-01-01
Journal of Applied Polymer Science
Abstract:Branched poly(butylene succinate) (PBS) copolymers were synthesized, from succinic acid (SA), 1,4-butanediol (1,4-BD), and 1,2-octanediol (1,2-OD) through a two-step process containing esterification and polycondensation, with different mole fractions of 1,2-OD segments. The branched PBS copolymers were characterized with H-1-NMR, differential scanning calorimetry (DSC), wide angle X-ray diffraction (WAXD), thermogravimetric analysis (TGA), dynamic rheological testing, and tensile properties analysis. The results of DSC and WAXD show that, with the increasing of the 1,2-OD segments content, the glass transition temperature (T-g), melting temperature (T-m), crystallization temperature (T-c), and the degree of crystallinity (X-c) decrease. While the crystal structure of PBS does not change by introducing 1,2-OD segments. The results of TGA and dynamic rheological testing indicate that the thermal stability of neat PBS is improved with the addition of 1,2-OD segments. The incorporation of 1,2-OD segments has some effects on the rheological properties of PBS, such as complex viscosities ( vertical bar eta* vertical bar), storage modulus (G'), and loss modulus (G ''). Tensile testing demonstrates that the elongation at break is improved significantly with increasing 1,2-OD segments content, but without a notable decrease of tensile strength. (C) 2010 Wiley Periodicals, Inc. J Appl Polym Sci 117: 2538-2544, 2010