In-situ imaging to elucidate on scaling and wetting in membrane distillation

I-Min Hsieh,Bosong Lin,Hadis Matinpour,Mahdi Malmali

DOI: https://doi.org/10.1016/j.desal.2024.117393

IF: 11.211

2024-02-03

Desalination

Abstract:Membrane distillation (MD) has received enormous attention for its potential in desalination of hypersaline brine. Mineral scaling on the membrane surface has yet remained a significant challenge that has limited MD's large-scale implementation and commercialization. Scaling reduces the membrane throughput and will eventually lead to scaling-induced membrane wetting. In this work, a real-time, in-situ, and non-invasive apparatus was designed and established to monitor the scaling phenomenon in vacuum MD (VMD). This apparatus consisted of two optical imaging cameras located on the feed and permeate sides, an in-line turbidity meter, and an in-line conductivity meter to track the formation of the crystals and deposition on the membrane surface. A major finding was that we could distinguish the onsets of heterogeneous nucleation and bulk phase crystallization using imaging and turbidity reading, respectively. Conductivity measurement was also used to indirectly verify these stages of scaling identified via imaging and turbidity. Scaling behavior for gypsum, calcite, and silica were studied. For gypsum, as a representative scalant, large needle-like gypsum crystals were formed during the heterogeneous nucleation and growth phase; this was later followed by the bulk crystallization phase, in which smaller crystals deposited on the surface and led to severe flux decline and eventually membrane wetting. The scattered calcite scaling on the membrane surface had an insignificant influence on the MD flux. For silica, 30 % flux decline was observed due to the deposition of floating silica nanoparticles on the membrane surface. Both calcite and silica scaling did not lead to membrane wetting within the period of the MD test. The morphologies of scalants obtained from real-time imaging were confirmed by SEM, and their crystalline structure was further evaluated by XRD. It was found that the concentration polarization was effectively mitigated by hydrodynamics, which played an important role in mitigating heterogeneous nucleation and crystal growth; the deposition of floating crystals formed during bulk phase crystallization was also influence by flow hydrodynamics.

engineering, chemical,water resources