A novel efficient Mn4+-activated Ba2YTaO6 far-red emitting phosphor for plant cultivation LEDs: Preparation and photoluminescence properties

Wei Li,Nan Ma,Qi Sun,Shaoying Wang,Zongjie Zhang,Balaji Devakumar,Xiaoyong Huang

DOI: https://doi.org/10.1016/j.jlumin.2020.117621

IF: 3.6

2020-12-01

Journal of Luminescence

Abstract:<p>Novel efficient Ba₂YTaO₆:Mn⁴⁺ (BYT:Mn⁴⁺) far-red emitting double-perovskite phosphors for plant cultivation LEDs were reported in this article. These phosphors were successfully synthesized via a traditional high-temperature solid-state reaction method, and their crystal structure, luminescence properties, fluorescence decay lifetimes, Commission Internationale de l´Eclairage (CIE) chromaticity coordinates, internal quantum efficiency, and thermal stability have been systematically investigated. XRD Rietveld refinement demonstrated that the BYT:Mn⁴⁺ compound crystallized into cubic crystal system with <em>Fm</em>fx1<em>m</em> space group, and the lattice parameter were <em>a</em> = <em>b</em> = <em>c</em> = 8.445(7) Å, <em>α</em> = <em>β</em> = <em>γ</em> = 90^o, and <em>V</em> = 602.231(10) Ǻ³. Interestingly, the obtained samples showed an intense far-red emission band centered at 690 nm under excitation of 360 nm, which matched well with the absorption band of phytochrome P_FR. In BYT:Mn⁴⁺ phosphors, the Mn⁴⁺ ions occupied the TaO₆ octahedron by replacing the Ta⁵⁺ site, and the optimal doping concentration of Mn⁴⁺ ions was determined to be 0.4 mol%. The CIE chromaticity coordinates and internal quantum efficiency of BYT:0.4%Mn⁴⁺ phosphors were (0.7283, 0.2717) and 41.5%, respectively. In addition, when the temperature reached at 423 K, the emission intensity of BYT:0.4%Mn⁴⁺ phosphors remained 37% of that at 303 K. Therefore, all of these investigations demonstrated that BYT:Mn⁴⁺ phosphors could be used as potential far-red emitting phosphors for plants cultivation LEDs.</p>

optics