Strength degradation of 42CrMo steel in a thermal field and its characterization method

Sheng Liu,Chong Cui,Da Zhang,Chuang Wang,Xiao Wang

DOI: https://doi.org/10.1016/j.matlet.2020.128031

IF: 3

2020-09-01

Materials Letters

Abstract:<p>The effect of thermal temperature on microstructures and mechanical properties of 42CrMo steel was reported in this paper. A sharp strength degradation in this material occurs as the thermal aged temperature rise to 600℃, and the lath microstructure turned into a fine and granular tempered sorbite. The mechanism of the strength degradation due to C and Cr element precipitating that caused the matrix softening. Besides, the magnetic parameters were sensitive to the microstructure change of 42CrMo steel, which showed good regularity as compared with its strength variation. The results manifested that the electromagnetic technique is an effective method to assess the thermal degradation of 42CrMo steel.</p>

materials science, multidisciplinary,physics, applied

What problem does this paper attempt to address?

This paper aims to study the strength degradation of 42CrMo steel in a thermal field and its characterization methods. Specifically, the paper focuses on the following issues:

1. **The impact of thermal aging on the microstructure and mechanical properties of 42CrMo steel**: The study found that when the thermal aging temperature rises to 600°C, 42CrMo steel exhibits a significant decrease in strength. The changes in microstructure are manifested as the transformation of lath martensite into fine granular tempered sorbite.

2. **The mechanism of matrix softening caused by element precipitation**: The research indicates that at high temperatures, C and Cr elements precipitate from the matrix, leading to matrix softening, which in turn causes a decrease in strength.

3. **Evaluation of the effectiveness of electromagnetic technology**: The paper also explores the effectiveness of electromagnetic technology in assessing the thermal degradation of 42CrMo steel. Experimental results show that magnetic parameters (such as coercivity, hysteresis loop area, and remanence) have a good correlation with changes in material strength, indicating that electromagnetic technology can effectively assess the degree of thermal degradation of 42CrMo steel.

In summary, through experiments and analysis, this paper reveals the mechanism of strength degradation of 42CrMo steel at high temperatures and verifies the application value of electromagnetic technology in assessing this degradation phenomenon.