Anchoring highly dispersed metal nanoparticles by strong electrostatic adsorption (SEA) on dealuminated Beta zeolite for catalysis
Run Zou,Gabriel Bramley,Shanshan Xu,Sarayute Chansai,Monik Panchal,Huanhao Chen,Yangtao Zhou,Pan Gao,Guangjin Hou,Stuart Holmes,Christopher Hardacre,Yilai Jiao,Andrew J Logsdail,Xiaolei Fan
DOI: https://doi.org/10.1039/d3cy01334k
IF: 6.177
2023-11-29
Catalysis Science & Technology
Abstract:Zeolites possessing adjustable defect sites (e.g., isolated silanol and silanol nests) have emerged as ideal catalyst supports to stabilise metallic species (e.g., clusters and nanoparticles). However, enhancement of the interactions that occur between framework defects and the metallic adsorbates, as well as the associated mechanisms, are still needed to advance catalyst design. Herein, highly dispersed Ni nanoparticles (NPs) are prepared on a defect-rich dealuminated Beta (deAl-Beta) zeolite through strong electrostatic adsorption (SEA), which enables strong interactions between the electronegative deAl-Beta and cationic metal ammine complexes (e.g., Ni(NH3)62+) via the framework silanol nests. The interactions effectively stabilise the ultrasmall metal NPs after reduction in H2 at 500 °C. Ni NPs with the diameter of 1.9 ± 0.2 nm form when using Ni(NO3)2 as precursor, and perform well in CO2 methanation. The catalyst performance is stable after 40 h of continuous testing at 400 °C. Comparative studies on Ni catalysts prepared by impregnation (IM) and SEA, or supported on deAl-Beta with less silanol defects (i.e., calcinated deAl-Beta), show that the ultrasmall metallic Ni NPs synthesised on defect-rich deAl-Beta via SEA provide better CO2 methanation activity. The mechanism of the SEA synthetic process was further elucidated by ex situ XAFS, in situ DRIFTS, and DFT. XAFS of the as-prepared Ni catalysts (i.e., unreduced) indicates that SEA leads to the exchange of anions in Ni precursors (e.g., Cl− and NO3−) to form Ni(OH)2, while in situ DRIFTS of catalyst reduction shows a significant decrease in the signal of IR bands assigned to the silanol nests (at ~960 cm−1), which could be ascribed to the strong interaction between Ni(OH)2 and silanol nests via SEA. DFT calculations show that the interactions between the framework and complexes are generally stronger during the SEA synthesis, with metal complexes binding stronger to the deprotonated framework, by up to 150 kJ mol−1, when compared to adsorption on the fully protonated silanol nests (i.e., IM synthesis). The results provide new opportunities for preparing highly dispersed metal catalysts using defect-rich zeolitic carriers for catalysis.
chemistry, physical