Synthesis and characterization of PANI-CZF nanocomposites for enhanced electromagnetic interference shielding

G. Harisha,D. R. Rangaswamy,R. Thejas,C. Devaraja,M. Revanasiddappa,M. V. Murugendrappa,K. M. Rajashekara

DOI: https://doi.org/10.1007/s10854-024-12086-6

2024-02-24

Journal of Materials Science Materials in Electronics

Abstract:The Zn 0.5 Cu 0.5 Fe 2 O 4 nano ferrites were prepared by the solution combustion method using aloe vera gel. The polyaniline-Zn 0.5 Cu 0.5 Fe 2 O 4 nano ferrite composites were prepared by Ex-situ polymerization method with different weight percentage ratio. The prepared samples were examined by X-Ray diffraction, SEM, EDAX, BET, TEM, VSM and Impedance analyser to investigate their structural, morphological, elemental analysis, average pore size and the porosity, magnetic, and dielectric properties, respectively. The cubic spinel structure was confirmed by X-ray diffraction patterns. Addition of PANI to zinc-copper nano ferrite exhibits shift in crystalline peaks towards larger angle. The existence of spherical and clumped particles was revealed by SEM examination. The retentivity and coercivity are determined and the magnetic moment values were decreases with increase in PANI to the ferrite nanocomposites. The ac conductivity constant at lower frequency and there is a sudden increase and decrease in its value as a function of frequency shows resonance behaviour. The CZF-1 (CZF 30%) composite shows highest ac conductivity and dielectric constant. The electromagnetic shielding interference studies were conducted for S-band frequency. The CZF-1 (CZF 30%) nano composite shows highest shielding effectiveness as compared to other composite in the frequency range 2 to 3 GHz. The experimental result showed that these materials are used for applications in electromagnetic interference shielding.

engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied

What problem does this paper attempt to address?

### What problem does the paper attempt to solve?

The paper primarily investigates the synthesis of polyaniline (PANI) and copper-zinc ferrite (Cu0.5Zn0.5Fe2O4) nanocomposites and their application in electromagnetic interference (EMI) shielding.

#### Research Background
With the development of electronic devices, the impact of electromagnetic interference (EMI) on various equipment has become increasingly significant, especially in fields such as medical devices, implantable devices, and autonomous vehicles. To mitigate the effects of EMI, it is necessary to develop efficient and lightweight absorbing materials. These materials should possess two fundamental characteristics: wave attenuation capability and impedance matching. Additionally, factors such as low weight, thinness, high mechanical strength, wide absorption reflection loss range, and environmental resistance need to be considered.

#### Research Content
1. **Material Synthesis**: Cu0.5Zn0.5Fe2O4 nano ferrite was synthesized by solution combustion method, and PANI-Cu0.5Zn0.5Fe2O4 nanocomposites with different ratios were prepared by in-situ polymerization.
2. **Characterization Analysis**: The materials were characterized in detail using X-ray diffraction (XRD), scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX), transmission electron microscopy (TEM), and vibrating sample magnetometry (VSM).
3. **Performance Testing**: The electromagnetic shielding effectiveness of these nanocomposites was studied, particularly their performance in the S-band frequency range.

#### Main Findings
- The addition of PANI caused changes in the lattice structure of Cu0.5Zn0.5Fe2O4 nano ferrite, leading to a shift of the crystal plane peaks to higher angles.
- The hysteresis loops showed that the saturation magnetization increased with the increase in PANI content.
- In terms of electromagnetic shielding performance, the CZF-1 (containing 30% PANI) composite material exhibited the best shielding effectiveness in the 2 to 3 GHz frequency band.
- The composites showed higher AC conductivity in the low-frequency region and exhibited resonance behavior in the high-frequency region.

In summary, the paper aims to explore the potential application of PANI-Cu0.5Zn0.5Fe2O4 nanocomposites in the field of electromagnetic interference shielding through their preparation and study.