Ion Selectivity of Chromium Hydroxide and Chromium-Nickel Mixed Hydroxide Precipitate Membranes

N. Sato,M. Sakashita

DOI: https://doi.org/10.3323/JCORR1974.25.1_3

1976-01-15

Abstract:Measurements of membrane potentials arising across chromium hydroxide and chromium nickel mixed hydroxide precipitate membranes have been carried out to estimate the ion selectivity. The chromium hydroxide precipitate membrane showed a high selectivity for anions in electrolyte solutions of neutral pH. The transport number of anions was evaluated to be 0.96-0.95 in sodium chloride, nitrate, and perchlorate solutions. The fixed ion concentration on the membrane characterizing anion exchanger was determined to be about 0.1g-equiv./l by comparing the experimental membrane potentials with the theoretical values derived from the fixed charge theory of membranes. In sodium hydroxide solution, the transport number of OHions through the membrane was not constant but increased with decreasing solution pH. The order of the selectivity for anions determined with the biionic potentials across the chromium hydroxide precipitate membrane was Cl->Br->NO-3>I->ClO4-. This order of the selectivity differs significantly from the selectivity for the nickel hydroxide precipitate membrane. The biionic potential across the mixed hydroxide precipitate membranes of chromium and nickel shifted from that of nickel hydroxide to that of chromium hydroxide as the chromium concentration increased. The anion permeability estimated from the membrane potential arising across the biphase hydroxide membrane was very much smaller for the chromium hydroxide than for the nickel hydroxide precipitate membrane. This suggests that chromium is enriched on the surface of hydroxide particles constructing the mixed membranes.

Chemistry