A Thermally and Chemically Stable Copper(II) Metal–Organic Framework with High Performance for Gas Adsorption and Separation

Zhi Long,Pu Xu Liu,Zhong Yi Liu,Jia Jun Wang,Li Bo Li,Li Tian,Zhi Long Ma

DOI: https://doi.org/10.1021/acs.inorgchem.1c00357

IF: 4.6

2021-04-16

Inorganic Chemistry

Abstract:A versatile microporous metal–organic framework (MOF), {[Cu(TIA)]·1.5CH₃OH}_<i>n</i> (<b>Cu-1</b>), was successfully obtained via the solvothermal reaction of cuprous(II) salt with the bifunctional ligand 3-(1<i>H</i>-1,2,4-triazol-1-yl)isophthalic acid. Single-crystal X-ray diffraction studies indicate that <b>Cu-1</b> contains an <i>apo</i> three-dimensional skeleton and two types of one-dimensional channels. The framework of <b>Cu-1</b> has excellent acid-alkali resistance and thermal stability, which is stable in a pH = 2–13 aqueous solution and an 260 °C air environment. In addition, the microporous copper MOF shows very high uptakes of CO₂ (180 cm³·g^–1) and C₂H₂ (113 cm³·g^–1) at 273 K and displays excellent adsorption selectivity for small molecular gases. The ideal adsorbed solution theory selectivity values for C₂H₂/C₂H₄, CO₂/CH₄, and CO₂/N₂ are 2, 9, and 22 at 298 K, respectively. At the same time, breakthrough experiments for CO₂/CH₄, CO₂/N₂, and C₂H₂/C₂H₄ were further conducted to verify the efficient separation performances.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.inorgchem.1c00357?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.inorgchem.1c00357</a>.Computational methods, physical measurements, synthesis of H₂TIA, crystallographic data, PXRD, TGA, other sorption properties, and calculation of <i>Q</i>_st (<a class="ext-link" href="/doi/suppl/10.1021/acs.inorgchem.1c00357/suppl_file/ic1c00357_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

chemistry, inorganic & nuclear

What problem does this paper attempt to address?

The paper primarily focuses on developing a novel type of Metal-Organic Framework (MOF) material, named {[Cu(TIA)]·1.5CH3OH}n (Cu-1), for gas adsorption and separation. Cu-1 is synthesized through a solvothermal reaction from copper(II) salts and the bifunctional ligand 3-(1H-1,2,4-triazol-1-yl)isophthalic acid. Single-crystal X-ray diffraction studies indicate that Cu-1 possesses a three-dimensional framework structure with two types of one-dimensional channels, demonstrating excellent acid-base stability and thermal stability, remaining stable in aqueous solutions with pH=2 to 13 and in air at 260°C.

Cu-1 exhibits extremely high adsorption capacities for carbon dioxide (CO2) and acetylene (C2H2) at low temperatures, which are 180 cm3·g−1 and 113 cm3·g−1, respectively, and shows good selective adsorption performance for small molecular gases. Theoretical calculations reveal that the selectivities of Cu-1 for C2H2/C2H4, CO2/CH4, and CO2/N2 are as high as 2, 9, and 22, respectively.

To verify the efficient separation performance of Cu-1, the paper further conducted breakthrough experiments, confirming its effective separation capability in mixtures of CO2/CH4, CO2/N2, and C2H2/C2H4. Therefore, Cu-1 could not only potentially become an ideal material for capturing post-combustion CO2 from fuel gases but is also suitable for the deep purification of ethylene in natural gas purification and industrial production, removing trace amounts of acetylene.

In summary, the study has developed a multifunctional MOF material, Cu-1, with outstanding chemical and thermal stability. It shows great potential in CO2 capture and light hydrocarbon separation, and is expected to be applied in the field of industrial gas purification.