Abstract:Melamine pretreated with hydrochloric acid was mixed with diatomite-based porous ceramics ( Ф 18 × 6 mm in size) and then heated from room temperature through an intermediate holding temperature up to 550 °C and calcined for 2 h to obtain g-C 3 N 4 /diatomite-based porous ceramic composites (xHCN/D, x = 310, 355, 400, representing the holding temperature in the intermediate stage). The samples were characterized by XRD, FT-IR, SEM, UV–Vis, PL, etc.. Rhodamine B (RhB) solution was used as the target pollutant to evaluate the photocatalytic activity of the samples. The results show that the phase composition of xHCN/D composites included g-C 3 N 4 and those in diatomite-based porous ceramic. The photocatalytic activity of xHCN/D composites were better than that of 355CN/D composite synthesized under the same condition as 355HCN/D but using pristine melamine, although the loading rates of g-C 3 N 4 on xHCN/D were much smaller than that on 355CN/D. The photocatalytic activity of xHCN/D changed with the variation of x, and 355HCN/D exhibited the optimum photocatalytic performance as well as excellent cycling stability and recoverability. 355HCN/D (1 g) degraded 86.74% of RhB molecules (2 mg/L, 100 mL) in 200 min, whose reaction rate constant was 1.45 times that of 355CN/D. In addition, the photocatalytic activity of 355HCN/D particles (3–4 mm in size) was superior to that of 355HCN/D disc. The enhanced UV–visible light absorption ability, narrowed band gap and the decreased photo-generated electron-hole recombination rate of 355HCN/D were ascribed to the significantly reduced size and appropriate amount of g-C 3 N 4 sheets loaded uniformly on the surface of diatomite-based porous ceramic, due to the synergistic action of acid-treating to melamine and holding at an intermediate temperature. This work provides a strategy for preparing high performance photocatalysts with a facile separation and recycle ability.

One-pot synthesis of g-C3N4/diatomite composite with nitrogen vacancies for enhanced photocatalytic activity

Preparation of g-C3N4/diatomite composite with improved visible light photocatalytic activity

Graphitic Carbon Nitride Facilely Modified with Pyromellitic Diimide with Enhanced Photocatalytic Activity and Good Selectivity Towards the Photodegradation of Cationic Dyes

Enhanced Photocatalytic Performance of Broken Hollow Tubular Carbon Nitride Modified with Nitrogen Defects and Hydroxyl Groups for Pollutant Degradation and Hydrogen Production

Uracil-Doped Graphitic Carbon Nitride For Enhanced Photocatalytic Performance

Synthesis and photocatalytic performance of composite g-C3N4 with functionalized multi-walled carbon nanotubes

One-step Preparation of Sulfur-Doped Porous G-C3n4 for Enhanced Visible Light Photocatalytic Performance.

Construction of a facile separation and recycle photocatalyst: g-C 3 N 4 /diatomite-based porous ceramic composite

One-step synthesis of S-doped and nitrogen-defects co-modified mesoporous g-C3N4 with excellent photocatalytic hydrogen production efficiency and degradation ability

Optimal Structure and Photocatalytic Performance of C3N4@TiO2 Composite by Controlling the Molar Ratio of Components

Growth of G-C3n4 on Mesoporous TiO2 Spheres with High Photocatalytic Activity under Visible Light Irradiation

Enhanced photocatalytic performance and mechanism of N-deficiently porous g-C 3 N 4 in organic pollutant degradation

Preparation of g-C3N4/vermiculite composite with improved visible light photocatalytic activity

Enhancing photoactivity of defective g-C3N4 via self-polarization effect of tourmaline for CO2 reduction

High temperature promoted synthesis of graphitic carbon nitride with porous structure and enhanced photocatalytic activity

Construction of g-C3N4 with three coordinated nitrogen (N3C) vacancies for excellent photocatalytic activities of N2 fixation and H2O2 production

Investigation on g-C3N4/rGO/TiO2 nanocomposite with enhanced photocatalytic degradation performance

Synthesis of G-C 3 N 4 /cqds Composite and Its Photocatalytic Degradation Property for Rhodamine B

Synthesis and photocatalytic performance of g-C3N4/MeTMC-COP composite photocatalyst

Research on preparation and performance of g-C3N4/kaolinite composite by chemical impregnation combined with thermal polymerization method

SYNTHESIS AND PHOTOCATALYTIC PERFORMANCE OF g-C3N4 COMPOSITES