Abstract:Polystyrene (PS) is a widely used building insulation material with good mechanical strength and strong temperature adaptability. However, PS itself is highly flammable and displays poor flame retardancy. At present, building fires caused by organic external wall thermal insulation materials prepared from PS represent a new fire hazard. In this study, the addition of an intumescent flame retardant (IFR) to reduce the flammability of PS was achieved. Using melamine (MEL), acrylonitrile-styrene-acrylate (ASA), and phytic acid (PA) as raw materials, a new type of flame retardant (MAP) was prepared by an electrostatic self-assembly method and was introduced to modify PS. Its effect on the flammability of PS composites was also investigated. The flammability of the PS composites was characterized using the limiting oxygen index (LOI) and vertical combustion. The effect of MAP on the morphology of the carbon layer formed from polymer decomposition was studied using scanning electron microscopy (SEM). By adding MAP to a PS/20%N-IFR flame-retardant composite, the flame-retardant property was significantly improved, the limiting oxygen index reached 37, and the vertical combustion reached a V-0 level. The fire performance index (FPI) of the PS/20%N-IFR composite reached 0.0054, which was significantly higher than that of the control PS (0.037) as determined by the cone calorimetry test. The SEM results showed that the introduction of MAP can increase the density of the carbon layer after combustion. The heat release rate for combustion was reduced. In addition, the mechanical properties of the PS/20%N-IFR composites were compared with those with no flame retardant. The tensile strength of the PS/20%N-IFR composite was 26.1 MPa and the elongation of the PS/20%N-IFR composite remained at 2.2%. The PS/20%N-IFR composite displayed better flame retardancy than the untreated material and good mechanical properties. The presence of MAP prevented the heat and oxygen transfer and interrupted the releasing of flammable products, thus protecting the PS from burning. This flame-retardant material may find broad applications in building insulation materials.

Examining the combustion hazards of polyacrylonitrile-based stabilizing fiber insulation with cellulose adhesive

Study of Thermal and Mechanical Behaviors of Flame Retardant Polystyrene-Based Nanocomposites Prepared Via In-Situ Polymerization Method

Biomass intumescent flame retardant polyacrylonitrile composite: flame retardancy, smoke suppression and recycling

Preparation of flame retardant, smoke suppression and reinforced polyacrylonitrile composite fiber by using fully biomass intumescent flame retardant system and its sustainable recycle application

Preparation of flame retardant and antibacterial polyacrylonitrile composites based on modified microcrystalline cellulose loaded silver nanoparticles

Preparation of a New Type of Expansion Flame Retardant and Application in Polystyrene

Thermal and Combustion Properties of Biomass-Based Flame-Retardant Polyurethane Foams Containing P and N

Synthesis of a novel biomass-based flame retardant featuring vinyl-terminated chemical cross-linking and application in flame retardancy, smoke suppression, toxicity reduction and mechanical enhancement of PAN composite fibers

Cellulose Nanocrystals/Melamine/Phytic Acid Nanocomposites as Thermally Insulating and Flame-Retardant Structural Materials

Tunable Thermal, Flame Retardant and Toxic Effluent Suppression Properties of Polystyrene Based on Alternating Graphitic Carbon Nitride and Multi-Walled Carbon Nanotubes

One-pot complexation of phytic acid and polyethyleneimine on cellulosic microfibers towards insulative and flame-resistant foam

Gas evolution in self-extinguishing and insulative nanopolysaccharide-based hybrid foams

Fabrication of Rigid Isocyanate-Based Polyimide Foam Achieved Excellent Use Safety via Synergy between Expandable Graphite and Phosphorus-Containing Polyol

Synthesis of bio-based phosphorus-nitrogen hybrid cellulose nanocrystal flame retardant for improving of fire safety of epoxy resin

Preparation of Flame Retardant Polyacrylonitrile Fabric Based on Sol-Gel and Layer-by-Layer Assembly

Impact of Cellulose Modification by Expandable Graphite and Carbon Nanotubes on Flammability and Thermal Properties

A Green Synthesis Strategy for Liquid Microcapsule Flame-Retardant Polyurethane Foam: Lowering Consumer Health Risks from Flame Retardant Inhalation and Ensuring Long-lasting Fire Safety

Enhancing flame retardancy of polyphenylene sulfide nanocomposite fibers by the synergistic effect of catalytic crosslinking and physical barrier

Preparation of Phosphorus/Hollow Silica Microsphere Modified Polyacrylonitrile-Based Carbon Fiber Composites and Their Thermal Insulation and Flame Retardant Properties

Polypyrrole combined with phenylzirconium phosphate loaded carbon spheres for reinforcing flame protection of composite coatings

Bioinspired sustainable cellulose-based nanocomposites with remarkable flame-retardant performance