Low-temperature Synthesis of High Entropy Amorphous Metal Oxides (HEOs) for Enhanced Oxygen Evolution Performances

Arpeeta Hota,Jiban Krushna Das,Prasanna Kumar Panda,Asim Abdallah Mohammed,Avijit Biswal,Benadict Rakesh,Bankim Chandra Tripathy
DOI: https://doi.org/10.1039/d4dt00074a
IF: 4
2024-01-31
Dalton Transactions
Abstract:The rational design of multiple metal ions to high entropy oxide electrode material via a single-step hydrothermal process is applicable to the evolution of oxygen molecules (O2) through simple water electrolysis. The cost-effectiveness, high performance, and durable nature are the key factors of non-precious high entropy multiple metal-based electrocatalysts and be used as replaceable catalysts than precious ones. This work portrays a low-temperature synthesis of cauliflower-type morphology of high-entropy amorphous metal oxide and their electrochemical performances towards oxygen evolution reaction (OER) have been investigated. The multiple metal ions (Mn2+, Fe3+, Co2+, Ni2+, Cu2+) oxide electrode material shows an acceptable oxygen evolution reaction (OER) with an overpotential (290 mV) at the current density of 10 mA/cm2 and a lower Tafel slope value of 85 mV/dec, respectively. Moreover, the 20 h durability test with negligible change in overpotential shows the efficacy of the modified electrode material in harsh alkaline media. The observed electrochemical results towards OER correspond to the amorphous nature of the active material that displayed cauliflower-type morphology, having a large specific surface area (240 m2 g-1) and providing higher electrochemical active sites as well. Consequently, the post-stability characterization study (such as PXRD, FESEM, TEM, and XPS) gives more informative results to understand the post-structural and morphological results of the high entropy amorphous metal oxide.
chemistry, inorganic & nuclear
What problem does this paper attempt to address?