Abstract:Co and Cu co‐doped Ni‐ferrite Ni1‐xCoxFe2‐yCuyO4 nanocrystals (NCs) are synthesized via a facile micro‐emulsion method. Physio‐chemical characterizations reveal significant enhancements: saturation magnetization increases from 31.32 to 50.75 emu/g, BET surface area increases from 52 to 104 m2/g and coercivity rises from 218.76 to 406.82 Oe. Moreover, under solar light, co‐doped materials exhibit a remarkable 94.14% removal of crystal violet (CV) dye compared to 38.044% for un‐doped materials. Herein, we have synthesised cobalt (Co) and copper (Cu) co‐doped Ni‐ferrite Ni1‐xCoxFe2‐yCuyO4 nanocrystals (NCs) via the facile micro‐emulsion method. The materials were analysed for various physio‐chemical characterizations to investigate the co‐doping (Co and Cu) effects on magnetic, structural, electrical, photo‐catalytic properties. The structural analysis via Fourier Transform Infrared spectroscopy (FTIR) and X‐rays diffraction (XRD) showed the successful fabrication of Co and Cu co‐doped materials with cubic spinel geometry having a single phase, the crystallite size was observed in 15 to 24 nm range. The electrical response measured using current‐voltage (I–V) analysis showed good electrical features, the electrical resistivity declined from 6.85×107 Ohm.cm for un‐doped materials to 0.04×107 Ohm.cm for co‐doped materials, which was accredited due to the synergistic effects of Co and Cu metal cations in co‐doped Ni‐based ferrite structures. Magnetic investigation using VSM analysis showed increased saturation magnetization (Ms 31.32 to 50.75 emu/g) and coercivity (218.76 to 406.82 Oe) because of the higher magnetic responses of Co2+ions in the co‐doped spinel ferrite NCs. BET surface‐area analysis showed good porosity for co‐doped materials with an increased surface area of 52 to 104 m2/g on co‐doping. The Tauc's plot described the decline of band‐gap energies value (Egs) (1.99 eV) in co‐doped (x=y=0.56) materials as compared to (2.16 eV) of the un‐doped NiFe2O4 materials, which is due to more electrical responses of Co and Cu co‐dopant cations that possess higher energy levels, which can stabilize the charge carrier's species. Furthermore, the photo‐degradation using solar light showed good removal of crystal violet (CV) dye, which was almost 94.14 % by co‐doped material; however, by un‐doped material, it was 38.044 %. The scavenger experiment shows that the (OH⋅) hydroxyl radicals and (e−/h+) species play a prime role in the degradation of CV dye. Recycling and recoverability tests for five cycles' exhibited outstanding stability of the photocatalyst with only 1.7 % losses in activity. Overall, our results showed that co‐doped Ni1‐xCoxFe2‐yCuyO4 NCs materials exhibited enhancement in the magnetic, electrical, photo‐catalytic properties and a decline in band‐gap energy values as compared to un‐doped NiFe2O4, which might have potential use in magnetic and electrical devices as well as solar‐driven photo‐catalyst materials for the remediation of environmental pollution.

Cadmium oxide nanoparticles doped with nickel and silver: Photocatalytic activity for environmental remediation

Increased photodegradation of crystal violet dye using Ni and Zn codoped cadmium oxide nanoparticles

Experimental and DFT + U Investigations of the Cu1-xCdxO Nanoparticles Synthesized for Photocatalytic Degradation of Organic Pollutants: Environmental Application

NiO and Ag–Cd co-doped NiO nanoparticles: study of photocatalytic degradation of rhodamine B dye for wastewater treatment

Cobalt and holmium co-doped nickel ferrite nanoparticles: synthesis, characterization and photocatalytic application studies

Synergistic effect of Ni doping and oxygen vacancies on the visible light photocatalytic properties of Ag2O nanoparticles

Co+2, Ni+2 and Cu+2 incorporated Bi2O3 nano photocatalysts: Synthesis, DFT analysis of band gap modification, adsorption and photodegradation analysis of rhodamine B and Triclopyr

Enhanced photocatalytic and electrochemical performance of hydrothermally prepared NiO‐doped Co nanocomposites

Synthesis and Characterizations of Fe-Doped NiO Nanoparticles and Their Potential Photocatalytic Dye Degradation Activities

Impact of Co and Cu co‐doping on the Structural, Electrical, Magnetic and Solar Light Driven Photo‐Catalytic Properties of NiFe2O4 Nano‐crystals for Crystal Violet Dye Removal

Biogenic synthesis of Cd doped SrFe 2 O 4 nanoparticles using Datura metel leaves extract and its performance as Photocatalytic agent for mixed dyes and Electrochemical properties

Study the influence of silver and cobalt on the photocatalytic activity of copper oxide nanoparticles for the degradation of methyl orange and real wastewater dyes

Synthesis of nanostructured microspheres of NiCoO2 for photocatalytic dye degradation

Drastic Improvement in Catalytic, Optical and Visible-Light Photocatalytic Behavior of Cobalt and Nickel Doped TiO2 Nanopowder

Investigation on Structural, Morphological, Optical, Magnetic properties of CdO-CoFe 2 O 4 nanocomposites and their Photocatalytic Application

Effect of Cu2+ Ions Substitution on Structure and Photocatalytic Activity of CuxNi1−xFe2O4 Nanoparticles

A comparative analysis on the dye degradation efficiency of pure, Co, Ni and Mn-doped CuO nanoparticles

Enhanced Photocatalytic Degradation of Azo Dye by Metal co- doped ZnO Nanorods under Ultraviolet Light Irradiation

Impact of metal doping and non metal loading on the photocatalytic degradation of organic pollutants using tin dioxide catalyst under sunlight irradiation

Synthesis of Binary Metal Doped CuO Nanoarchitecture for Congo red dye Removal: Synergistic Effects of Adsorption and Mineralization Techniques

Effect of silver doping on structural and photocatalytic circumstances of ZnO nanoparticles