Perovskite-type catalyst for tetracycline abatement under dark ambient over a wide pH range
Afonso Henrique da Silva Júnior,Carlos Rafael Silva de Oliveira,Paulo Alexandre Durant Moraes,Leandro Pellenz,Selene Maria de Arruda Guelli Ulson de Souza,Antônio Augusto Ulson de Souza,Luciano da Silva,Adriano da Silva
DOI: https://doi.org/10.1007/s10971-024-06324-w
2024-02-25
Journal of Sol-Gel Science and Technology
Abstract:The alarming release of pollutants into aquatic ecosystems, particularly concerning the emission of antibiotics, demands attention. Tetracycline (TC) is a drug commonly identified in both industrial and residential wastewater. In this context, new perovskite-type catalysts are considered a relevant topic for antibiotic degradation in water. The focus on oxides with a perovskite-like structure is due to their impressive thermal stability, cost-effectiveness, enhanced oxygen mobility, and flexibility for structural modifications. In this study, perovskite-type catalyst based on strontium and copper was synthesized and successfully applied in the TC degradation in absence of light. The material was prepared via sol-gel using a temperature controlled jacketed reactor. Numerous characterization techniques were applied to infer the catalyst's chemical and morphological aspects (TEM, SEM, XRD, BET, FTIR, and EDX). The material presented a dense characteristic and low porosity aspects. Also, the specific surface area and average pore diameter measured for the catalyst were 0.572 m 2 ∙ g −1 and 37.76 nm, respectively. In the degradation tests, no substance was added to assist in the treatment, which obtained excellent removal percentages over a wide pH range. Degradation yields achieved for pHs 4, 6, 7, and 10 were 94.3, 92.8, 92, and 90.4%, respectively. In addition, studies on surface adsorption, stability, phytotoxicity, main active species, and intermediates to assess the catalyst's performance were realized.
materials science, ceramics