Abstract:Oxygen Evolution Reaction (OER) is a slow process; therefore, improved kinetics require catalytic active centers and higher charge transfer capacities. In the present study, a novel heterostructure made of nickel molybdenum sulfide and vanadium disulfide supported on nickel foam (NiMo 2 S 4 -VS 2 /NF) substrate is fabricated using a single-step hydrothermal process. The structural, morphological, elemental, and textural properties of the fabricated materials are confirmed via various analytical techniques. Furthermore, at the current density of 10 mA cm −2 , the observed overpotentials was approximately 318 mV corresponding to an OER in 1 M potassium hydroxide electrolyte. It also shows a lower Tafel slope of 78 mV/dec with large turnover frequency of 2.56 s −1 . The resulting NiMo 2 S 4 -VS 2 /NF showed enhanced charge transfer properties and frequent integrated active sites. Hence the remarkable activity of this catalyst is significantly influenced by the synergistic effect of these combined features and resulted in an efficient overall water splitting. This was ascribed to NiMo 2 S 4 which increases OER at the anode by providing active sites for oxidizing water molecules. In NiMo 2 S 4, Mo and S elements aid to maintain active sites and accelerate reaction kinetics, while Ni sites operate as electrocatalytic efforts for water oxidation. In general, VS 2 promotes hydrogen atom recombination into molecular hydrogen while also encouraging HER at the cathode via hydrogen atom adsorption. In general, NiMo 2 S 4 -VS 2 /NF is a suitable option for water splitting applications due to the close proximity of these two components within the structure of the catalyst, which enables charge transfer and surface reactions and also allow for effective OER. This unique approach for designing the catalyst and engineering the heterointerface is a promising strategy to develop novel and efficient OER catalysts.

Molybdenum Oxide/Nickel molybdenum oxide heterostructures hybridized active platinum Co-Catalyst toward Superb-Efficiency water splitting catalysis

N, P co-doped Ni/Mo-based multicomponent electrocatalysts in situ decorated on Ni foam for overall water splitting

Unique hybrid Ni 2 P/MoO 2 @MoS 2 nanomaterials as bifunctional non-noble-metal electro-catalysts for water splitting.

Construction of Ni4Mo/MoO2 heterostructure on oxygen vacancy enriched NiMoO4 nanorods as an efficient bifunctional electrocatalyst for overall water splitting

Sequential Electrodeposition of Bifunctional Catalytically Active Structures in MoO 3 /Ni–NiO Composite Electrocatalysts for Selective Hydrogen and Oxygen Evolution

Bifunctional catalysts of Ni nanoparticle coupled MoO2 nanorods for overall water splitting

Manganese cobalt sulfide/molybdenum disulfide nanowire heterojunction as an excellent bifunctional catalyst for electrochemical water splitting

Pt modified NiMoO 4 -GO/NF nanorods with strong metal-support interaction as efficient bifunctional catalysts for overall water splitting

Molybdenum and Vanadium-Codoped Cobalt Carbonate Nanosheets Deposited on Nickel Foam as a High-Efficient Bifunctional Catalyst for Overall Alkaline Water Splitting

Ni-Mo based metal/oxide heterostructured nanosheets with largely exposed interfacial atoms for overall water-splitting

A Janus cobalt nanoparticles and molybdenum carbide decorated N-doped carbon for high-performance overall water splitting

NiMo2S4-VS2 heterostructure on nickel Foam: A promising electrocatalyst for alkaline oxygen evolution reaction

Platinum Clusters Anchored Amorphous NiMo Hydroxide with Collaborative Electronic Transfer for Overall Water Splitting under High Current Density

Amorphous nickel-cobalt complexes hybridized with 1T-phase molybdenum disulfide via hydrazine-induced phase transformation for water splitting

Cobalt-molybdenum bimetallic phosphide grown in situ on nickel foam as a bifunctional electrocatalyst for efficient water splitting

Mo, V and M ( M =Mn, Fe, Co, Cu) Co-modulated Ni oxides in-situ derived from nickel foam as efficient electrocatalysts for alkaline hydrogen evolution and oxygen evolution

In situ evolved NiMo/NiMoO 4 nanorods as a bifunctional catalyst for overall water splitting

Heterostructured MoO2@MoS2@Co9S8 nanorods as high efficiency bifunctional electrocatalyst for overall water splitting

NiCo-LDHs derived NiCo2S4 nanostructure coated by MoS2 nanosheets as high-efficiency bifunctional electrocatalysts for overall water splitting

Designing layered arrangement of cobalt-molybdenum bimetallic phosphide particles with different sizes on Ni foam for efficient overall water splitting

Highly active Mo-modified NiCoP/NiCoN flower-like sphere: Controlled phase engineering for efficient water splitting