Novel synthesis of reduced PdO-WO 3 hybrids for enhanced photoelectrochemical water splitting

Fizza Siddique,Amara Nasir,Karolina Syrek,Grzegorz D. Sulka,Sergio Gonzalez-Cortes,Chuanbo Li,Xiaoming Zhang,Ewa Wierzbicka

DOI: https://doi.org/10.1016/j.jallcom.2024.177615

IF: 6.2

2024-11-24

Journal of Alloys and Compounds

Abstract:In this study, a novel synthesis approach for WO 3 nanoparticles and their hybrids is proposed, followed by an investigation of their photoelectrochemical performance for water splitting applications. The surface modification of WO 3 nanoparticles is carried out by immersing them in a Pd precursor solution, followed by calcination to obtain PdO-WO 3 hybrid nanoparticles. Subsequently, the PdO-WO 3 is reduced in a hydrogen (H 2 ) environment to prepare PdO x -WO 3-y hybrid material. XPS analysis revealed that H 2 reduction converts residual metallic Pd to PdH and simultaneously generates oxygen vacancy defects in WO 3 hybrid nanoparticles, as confirmed by EPR analysis. Additionally, TPR analysis further confirms the H 2 -induced reduction in the PdO-WO 3 hybrid at a lowered temperature of 150 °C. The optical band gap energy of PdO x -WO 3-y hybrid nanoparticles is slightly reduced (by 0.06 eV) compared to that of the PdO-WO 3 reference sample. Photoelectrochemical measurements were conducted to assess the impact of these tailored modifications on the performance of conventional PdO-WO 3 nanoparticles. The reduced PdO x -WO 3-y catalyst exhibits an approximatly ∼22 % improvement in incident photon-to-current conversion efficiency (IPCE), over the unreduced PdO-WO 3 The PEC efficiency improvement was attributed to the composite electronic structure changes introduced during the annealing process. Mott-Schottky measurements confirm that the reductive treatment consolidates the material's two distinct flat band potentials (E fb ) into with a single intermediate energy level and increases the charge carrier concentration. This study presents a straightforward method to generate oxygen vacancy defects in hybrid metal oxides and provides a convenient method for band gap engineering for photoelectrocatalytic applications.

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering