Multiresponsive MXene (Ti 3 C 2 T x )-Decorated Textiles for Wearable Thermal Management and Human Motion Monitoring

Chang Ma,Qi Yuan,Haishun Du,Ming-Guo Ma,Chuanling Si,Pengbo Wan

DOI: https://doi.org/10.1021/acsami.0c10750

2020-07-16

Abstract:Over the past few years, wearable electronics and smart textiles have seen tremendous growth in both academia and industries. However, it is still a challenge to prepare robust, flexible, wearable, and multiresponsive textile electronics. A newly blooming two-dimensional (2D) transition-metal carbide/nitride (MXene) is regarded as an ideal active material to build multifunctional electronics due to its intriguing properties. Herein, a hydrophobic and multifunctional textile composite (Si-MAP) was prepared by decoration of conductive MXene nanosheets onto air-laid paper, followed by wrapping with poly(dimethylsiloxane) (PDMS). These obtained smart textiles exhibited excellent electronic/photonic/mechanical triresponsive properties: Si-MAPs could reach high equilibrium temperatures (104.9 and 118.7 °C) under quite low power illumination (1.25 W cm^–2) and working voltage (4 V). The Si-MAP pressure sensor exhibited high sensitivity and rapid response time (30–40 ms), which can capture a wide range of human movements. Moreover, the thin PDMS layer not only rendered the textile composites hydrophobic but also improved the stability and adaptation for daily use. Remarkably, the hydrophobic Si-MAPs have maintained the advantages of breathability and washability, which make them suitable for wearing. Thus, this smart Si-MAP textile provides a reference for the study of the next generation of light, portable, and wearable textile-based electronic devices.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c10750?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c10750</a>.SEM images of the MAX phase and multilayered MXene (Figure S1); digital image of the Tyndall scattering effect (Figure S2); X-ray diffraction patterns (Figure S3); XPS spectra of MXene and details of Ti and F patterns (Figure S4); TEM image (Figure S5); SEM images (Figure S6); gas permeability (Figure S7); contact angle of Si-APs (Figure S8); digital images of AP and Si-MAP before and after immersion in ethylene blue aqueous solution (Figure S9); digital images for different kinds of stains on Si-MAPs (Figure S10); schematic diagram of the light-responsive experiment (Figure S11); conductive stability of Si-MAPs (Figure S12); schematic diagram of the electrothermal experiment (Figure S13); equivalent circuit diagram of the Si-MAP-based pressure sensor (Figure S14); durability characteristics tests of the Si-MAP sensor for 5000 cycles (Figure S15) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c10750/suppl_file/am0c10750_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

materials science, multidisciplinary,nanoscience & nanotechnology