Abstract:The salt-frost damage characterization of multiple interfacial transition zones (ITZs) is one of the major concerns for further exploring the durability-related properties of recycled aggregate concrete (RAC) exposed to cold region. The actual service state of RAC structures is often coupled with multiple environments, leading to more complex freeze-thaw damage mechanisms in ITZs. This study adopted the simulant multiple ITZs of RAC specimens to investigate the damage evolution behavior of ITZs performance under the coupling actions of salt-frost cycles (SFT) and sustained compression loads. Effect of nano-silica (NS) and air-entraining agent (AE) on the saltfrost resistance strengthening for ITZs inside RAC was further explored. The apparent morphology and the relative dynamic elastic modulus (RDEM) of modified simulant multiple ITZs of RAC were measured to characterize the salt frost damage, and further the microstructural analysis including microhardness, laser scanning microscope (LSM) and SEM observation was conducted, aiming at revealing the salt-frost damage mechanisms of simulant modified ITZs inside RAC. The results indicate that the appropriate dosage of NS and AE could effectively reduce the salt-frost scaling of RAC by strengthening the internal microstructures. The RDEM of NSmodified RAC samples incorporating with AE was always higher than NS-modified RAC and non-modified RAC. After NS-modified, the minimum microhardness of old ITZs was increased by 10.2 % and the thickness was averagely reduced by about 10 mu m. The microhardness loss of modified RAC after SFT was relatively smaller. On the contrary, applying loading with higher compressive stress level markedly accelerates the salt-frost damage process of non-modified and modified ITZs. The results of SEM and LSM tests showed there is less salt-frost damage under sustained compression loads due to the denser microstructures of ITZs after synergistic modification by NS and AE. This is demonstrated by stronger bonding properties between original aggregate and old mortar and less elevation differences at old/new ITZs. Above all, this study explores the evolving trends of salt-frost damage and microstructure for simulant ITZs inside RAC under the coupling actions of sustained compression loads and SFT, which can provide some basis for the durability assessment of RAC structures exposed to cold region.

Salt-Frost Damage and Life Prediction of Nano-SiO2 Polypropylene Fiber Aeolian Sand Concrete

Mesoscale Simulation of Fatigue Behavior of Concrete Materials Damaged by Freeze-Thaw Cycles

Effects of Polypropylene Fibers on the Frost Resistance of Natural Sand Concrete and Machine-Made Sand Concrete

Experimental Study and Mechanism Analysis on Frost Resistance of Normal Performance Concrete under Different Environments

Multi-scale study on the durability degradation mechanism of aeolian sand concrete under freeze–thaw conditions

Two‐dimensional Rigid Body Spring Method Based Micro‐mesoscale Study of Mechanical Strengthening/damaging Effects to Concrete by Frost Action

Meso-Scale Mechanical Deterioration Of Mortar Subjected To Freeze Thaw Cycles And Sodium Chloride Attack

Experimental Examination of Electrical Characteristics for Portland Cement Mortar Frost Damage Evaluation

Experimental Evaluation of the Concrete Damage and Pore Characteristics under Salt-Freezing Cycles

Microstructure and life prediction model of steel slag concrete under freezing-thawing environment

A Numerical Study on Chloride Diffusion in Freeze-Thaw Affected Concrete

Salt-frost Damage Characterization of Simulant Multiple ITZs in Nano-Silica Modified Recycled Aggregate Concrete

Stress Analysis for Concrete Materials under Multiple Freeze-Thaw Cycles

Environmental Factors Influencing The Durability Of Concrete Structures In Frost Environments

Durability and Mechanical Properties of Nano-SiO2 and Polyvinyl Alcohol Fiber-Reinforced Cementitious Composites Subjected to Saline Freeze–Thaw Cycles

Salt-frost scaling resistance characteristics of nano silica-modified recycled aggregate concrete

Frost Durability of Self-Compacting Concrete Prepared with Aeolian Sand and Recycled Coarse Aggregate

Frost resistance of concrete mixed with nano-silica in severely cold regions

Numerical Simulation of the Effect of Freeze–Thaw Cycles on the Durability of Concrete in a Salt Frost Environment

Estimation of Ice Formation in Mortar Saturated with Sodium Chloride Solutions