Investigation of structural, dielectric, impedance, and conductivity properties of layered perovskites type compound: LiNdSnO4

Sushree Sangita Rout,Sudhansu Sekhar Hota,Debasish Panda,L. Biswal,Sushil Joshi,Alok Shukla,Pragyan Mohanty,Ram Naresh Prasad Choudhary

DOI: https://doi.org/10.1007/s10854-024-13600-6

2024-10-15

Journal of Materials Science Materials in Electronics

Abstract:The report in the article has emphasised the characterisation (structural analysis, sample microstructure, dielectric, impedance, and modulus) of a layered perovskite ceramic oxide LiNdSnO 4 (LNSO) prepared by solid-state reaction method. The compound formation and phase identification with multiphase are confirmed using X-ray diffraction (XRD). This XRD shows that the material contains LNSO as the predominant and minor impurity phases. The crystallite size and strain are calculated to be 106 nm and 0.001, respectively. SEM study shows that the grains formed in the sample are a combination of the big (~ 2.23 μm) and small grains (~ 0.95 μm). The ac conductivity follows the Jonscher's power law. The non-Debye type of relaxation mechanism and the hopping mechanism are shown by the shifting of the curve in the high-frequency zone in modulus spectra. The FT/IR study demonstrates the presence of a vibrational band in each element of the sample. The dielectric constant and loss increased sharply at 300 °C. The maximum activation energy (0.5598 eV) was found at a lower frequency. Nyquist spectrum indicates the presence of grain and grain boundary properties of the material. The semicircular behaviour of impedance spectra demonstrated that the material might be semiconducting. This study concluded that the compound is useful for NTCR thermistor devices.

engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied