Abstract:Densely accessible Fe‐N4 active sites in the hierarchical pore structure (FeSA‐SeNC‐meso/microporous) as a high‐loading Fe single‐atom catalyst (SAC) is achieved via a hierarchical‐pore‐stabilization strategy, which facilitates the adsorption of Fe3+ and stabilizes Fe atoms during pyrolysis. FeSA‐SeNC‐meso/microporous achieves high mass transfer and excellent oxygen reduction reaction (ORR) performance in both acidic and alkaline media. Metal single‐atom catalysts (M‐SACs) attract extraordinary attention for promoting oxygen reduction reaction (ORR) with 100% atomic utilization. However, low metal loading (usually less than 2 wt%) limits their overall catalytic performance. Herein, a hierarchical‐structure‐stabilization strategy for fabricating high‐loading (18.3%) M‐SACs with efficient ORR activity is reported. Hierarchical pores structure generated with high N content by SiO2 can provide more coordination sites and facilitate the adsorption of Fe3+ through mesoporous and confinement effect of it stabilizes Fe atoms in micropores on it during pyrolysis. High N content on hierarchical pores structure could provide more anchor sites of Fe atoms during the subsequent secondary pyrolysis and synthesize the dense and accessible Fe‐N4 sites after subsequent pyrolysis. In addition, Se power is introduced to modulate the electronic structure of Fe‐N4 sites and further decrease the energy barrier of the ORR rate‐determining step. As a result, the Fe single atom catalyst delivers unprecedentedly high ORR activity with a half‐wave potential of 0.895 V in 0.1 M KOH aqueous solution and 0.791 V in 0.1 M HClO4 aqueous solution. Therefore, a hierarchical‐pore‐stabilization strategy for boosting the density and accessibility of Fe‐N4 species paves a new avenue toward high‐loading M‐SACs for various applications such as thermocatalysis and photocatalysis.

Constructing highly utilizable Fe-N4 single-atom sites by one-step gradient pyrolysis for electroreduction of O2 and CO2

Mass production of high-performance single atomic FeNC electrocatalysts via sequenced ultrasonic atomization and pyrolysis process

Contracted Fe-N5-C11 Sites in Single-Atom Catalysts Boosting Catalytic Performance for Oxygen Reduction Reaction.

Double boosting single atom Fe-N<sub>4</sub> sites for high efficiency O<sub>2</sub> and CO<sub>2</sub> electroreduction

Double boosting single atom Fe–N4 sites for high efficiency O2 and CO2 electroreduction

Boosting Oxygen Reduction Catalysis with Fe–N4 Sites Decorated Porous Carbons Toward Fuel Cells

Creating Asymmetric Fe-N3C-N Sites in Single-Atom Catalysts Boosts Catalytic Performance for Oxygen Reduction Reaction

Building Atomic Scale and Dense Fe─N4 Edge Sites of Highly Efficient Fe─N─C Oxygen Reduction Catalysts Using a Sacrificial Bimetallic Pyrolysis Strategy

Hierarchical‐Pore‐Stabilization Strategy for Fabricating 18.3 wt% High‐Loading Single‐Atom Catalyst for Oxygen Reduction Reaction

Dual‐Shelled Hollow Leafy Carbon Support with Atomically Dispersed (n,s)‐bridged Hydroxy‐Coordinated Asymmetric Fe Sites for Oxygen Reduction

Fabricating high-loading Fe-N4 single-atom catalysts for oxygen reduction reaction by carbon-assisted pyrolysis of metal complexes

Restricted diffusion preparation of fully-exposed Fe single-atom catalyst on carbon nanospheres for efficient oxygen reduction reaction

Highly dispersed carbon-encapsulated FeS/Fe 3 C nanoparticles distributed in Fe-N-C for enhanced oxygen electrocatalysis and Zn-air batteries

Hierarchically porous Fe/N/S/C nanospheres with high-content of Fe-Nx for enhanced ORR and Zn-air battery performance

Creation of Densely Exposed and Cavity-Edged Single Fe Active Sites for Enhanced Oxygen Electroreduction

Constructing FeN4/graphitic nitrogen atomic interface for high-efficiency electrochemical CO2 reduction over a broad potential window

High Density Single Fe Atoms on Mesoporous N‐Doped Carbons: Noble Metal‐Free Electrocatalysts for Oxygen Reduction Reaction in Acidic and Alkaline Media

A Mn-N3 single-atom catalyst embedded in graphitic carbon nitride for efficient CO2 electroreduction

Porphyrinic Mof-Derived Rich N-Doped Porous Carbon with Highly Active Con4c Single Atom Sites for Enhanced Oxygen Reduction Reaction and Zn-Air Batteries Performance

Simultaneously Incorporating Atomically Dispersed Co‐Nx Sites with Graphitic Carbon Layer‐Wrapped Co9S8 Nanoparticles for Oxygen Reduction in Acidic Electrolyte

Atomically dispersed Ni anchored on polymer-derived mesh-like N-doped carbon nanofibers as an efficient CO2 electrocatalytic reduction catalyst