Abstract:Peroxymonosulfate (PMS), which is dominated by non-free radical pathway, has a good removal effect on organic pollutants in complex water matrices. In this article, a biodegradable cobalt-based catalyst (Co3O4/MoS2@NCS) was synthesized by a simple hydrothermal method with chitosan (CS) as nitrogen‑carbon precursor and doped with Cobaltic‑cobaltous oxide (Co3O4) and Molybdenum disulfide (MoS2), and was used to activate PMS to degrade dye wastewater. Electrochemical tests showed that Co3O4/MoS2@NCS exhibited higher current density and cycling area than MoS2@NCS and MoS2. In the Co3O4/MoS2@NCS/PMS system, the degradation rate of 30 mg·L-1 rhodamine B (RhB) reached 97.75 % within 5 min, and kept as high as 94.34 % after 5 cycles. Its rate constant was 1.91 and 8.37 times that of MoS2@NCS/PMS and MoS2/PMS, respectively. It had good complex background matrices and acid-base anti-interference ability, and had good universality and reusability. The degradation rate of methyl orange (MO) and methylene blue (MB) were more than 91 % within 5 min at pH 4.8. The experimental results demonstrated that MoS2-modified CS as a carrier exposed a large number of active sites, which not only dispersed Co3O4 nanoparticles and improved the stability of the catalyst, but also provided abundant electron rich groups, and promoted the activation of PMS and the production of reactive oxygen species (ROS). PMS was effectively activated by catalytic sites (Co3+/Co2+, Mo4+/Mo5+/Mo6+, CO, pyridine N, pyrrole N, hydroxyl group and unsaturated sulfur), producing a large number of radicals that attack RhB molecules, causing chromophore cleavage, ring opening, and mineralization. Among them, non-free radical 1O2 was the main ROS for RhB degradation. This work is expected to provide a new idea for the design and synthesis of environmentally friendly and efficient MoS2-modified cobalt-based catalysts.

Co/N co-doped carbonized wood sponge with 3D porous framework for efficient peroxymonosulfate activation: Performance and internal mechanism

Iron cobalt and nitrogen co-doped carbonized wood sponge for peroxymonosulfate activation: Performance and internal temperature-dependent mechanism

Co/N co-doped carbonaceous polyhedron as efficient peroxymonosulfate activator for degradation of organic pollutants: Role of cobalt

Well-dispersed cobalt nanoparticles encapsulated on ZIF-8-derived N-doped porous carbon as an excellent peroxymonosulfate activator for sulfamethoxazole degradation

Synergistic activation of peroxymonosulfate by 3D CoNiO2/Co core-shell structure biochar catalyst for sulfamethoxazole degradation

MnOx@N-doped carbon nanosheets derived from Mn-MOFs and g-C3N4 for peroxymonosulfate activation: Electron-rich Mn center induced by N doping

A novel Co-N-doped carbon catalyst to activate peroxymonosulfate for efficient removal of sulfamethazine: Role of singlet oxygen and high-valent cobalt-oxo species

Peroxymonosulfate activation by concave porous S/N co-doped carbon: Singlet oxygen-dominated non-radical efficient oxidation of organics

Peroxymonosulfate activation by Fe-Co-O co-doped graphite carbon nitride for degradation of sulfamethoxazole.

Peroxymonosulfate Activation by Co9S8@ S and N Co‐doped Biochar for Sulfamethoxazole Degradation

Bimetal organic framework/graphene oxide derived magnetic porous composite catalyst for peroxymonosulfate activation in fast organic pollutant degradation.

Heterogeneous activation of peroxymonosulfate by flower-like cobalt sulfide enhanced sulfamethoxazole degradation via non-radical pathways

Nitrogen, Sulfur and Oxygen Co-Doped Carbon-Armored Co/Co9S8 Rods (Co/co9s8@n-S-o-c) As Efficient Activator of Peroxymonosulfate for Sulfamethoxazole Degradation.

Enhanced activation of peroxymonosulfate through exfoliated oxygen-doping graphitic carbon nitride for degradation of organic pollutants

Degradation Of Sulfamethoxazole Using Peroxymonosulfate Activated By Cobalt Embedded Into N, O Co-Doped Carbon Nanotubes

High Efficient Activation of Peroxymonosulfate by Co9S8 Anchored in N, S, O Co-Doped Carbon Composite for Degradation of Sulfamethoxazole: Effect of Sulfur Precursor and Sulfur Doping Content

Porous 3D superstructure of nitrogen doped carbon decorated with ultrafine cobalt nanodots as peroxymonosulfate activator for the degradation of sulfonamides

High Efficient Activation of Peroxymonosulfate by Co <sub>9</sub>s <sub>8</sub> Anchored in N, S, O Co-Doped Carbon Composite for Degradation of Sulfamethoxazole: Role of Sulfur Precursor and Sulfur Doping Content

Electronic Structure Modulation and Peroxymonosulfate Activation Mechanism of N-doped MnCo2O4: A Study on the Efficient Catalytic Degradation of Sulfamethoxazole

Chitosan derived N-doped carbon anchored Co3O4-doped MoS2 nanosheets as an efficient peroxymonosulfate activator for degradation of dyes

Peroxymonosulfate activation by nanocomposites towards the removal of sulfamethoxazole: Performance and mechanism