Island-to-acicular alteration of second phase enhances the degradation resistance of biomedical AZ61 alloy

Long Liu,Haotian Ma,Chengde Gao,Cijun Shuai,Shuping Peng

DOI: https://doi.org/10.1016/j.jallcom.2020.155397

IF: 6.2

2020-09-01

Journal of Alloys and Compounds

Abstract:<p>The application of Mg–6Al–1Zn (wt.%, AZ61) alloy as biodegradable bone implant material is limited due to its too rapid degradation, which is largely related to the microgalvanic corrosion induced by the coarse island second phase in the alloy. In this study, cerium (Ce) was alloyed in AZ61 alloy by selective laser melting, aiming to enhance its degradation resistance. The microstructure characteristics were investigated by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The degradation behavior was studied by the electrochemical test and weight loss test. Besides, the mechanical properties and cytocompatibility of the alloy were also assessed. The results showed that Al preferentially reacted with Ce in the AZ61-Ce alloy because of the high electronegativity difference between Al and Ce and formed acicular Al₄Ce phase due to the oriented crystal growth. Meanwhile, the consumption of Al in forming Al₄Ce phase inevitably reduced the precipitation of island Mg₁₇Al₁₂ phase. Compared with island Mg₁₇Al₁₂ phase, the acicular Al₄Ce phase possessed much larger ratio of length to the cross-sectional area, leading to a higher electrical resistance. As a consequence, the island-to-acicular alteration of second phase greatly decreased the corrosion current density, thereby enhancing the degradation resistance by about 7 times. In addition, the AZ61-Ce alloy presented improved compressive strength owing to the strengthening effect of the acicular second phase, as well as favorable biocompatibility. The island-to-acicular alteration of second phase may provide a method for the development of high performance biomedical Mg alloys.</p>

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

The problem that this paper attempts to solve is the excessive degradation rate of magnesium alloy AZ61 when it is used as a degradable bone implant material. Specifically, the micro - galvanic corrosion caused by the coarse island - like second phase (Mg_17Al_12) in the AZ61 alloy accelerates the degradation process of the alloy, resulting in limited applicability in bone implant applications. To solve this problem, researchers added the rare earth element cerium (Ce) to the AZ61 alloy through selective laser melting technology, aiming to improve the degradation resistance of the alloy by changing the morphology of the second phase (from island - like to needle - like). Studies have shown that adding an appropriate amount of Ce can significantly reduce the corrosion current density of the alloy, thereby increasing the degradation resistance by about 7 times, and also improving the compressive strength and cell compatibility of the alloy. This provides a new method for developing high - performance biomedical magnesium alloys.