Effect of UV-induced crosslink network structure on the properties of polylactic acid/polybutylene adipate terephthalate blend

Xueyan Bian,Suju Fan,Gang Xia,John H. Xin,Shouxiang Jiang

DOI: https://doi.org/10.1007/s10965-024-04024-1

IF: 3.061

2024-06-21

Journal of Polymer Research

Abstract:Over the past few decades, biobased polylactic acid (PLA) has emerged as the most promising option to replace some of the fossil-based and nonbiodegradable polymers due to environmental concerns. In this study, a flexible polymer, polybutylene adipate terephthalate (PBAT) was blended with PLA to improve the toughness and flexibility of PLA, and the PLA/PBAT blend was further UV-induced to form crosslink structure. The results show that the flexibility and toughness of PLA could be significantly enhanced when PBAT was introduced, and the compatibility of PLA and PBAT could be enhanced by the development of a crosslink structure. Especially, the elongation at break and unnotched impact strength of ABT-UV30 (PLA/PBAT/triallyisocyanurate (TAIC) exposed to ultraviolet (UV) light for 30 min) was increased to 3.9 and 8.4 times of neat PLA. The glass transition temperature (Tg) of PLA was increased from 63.4 to 72.9 °C as the radiation duration was prolonged to 60 min. The melting point temperature of PBAT was also increased gradually until it eventually coincided with that of PLA. The thermalgravimetric analyzer thermograms show that a moderate amount of UV radiation can improve the thermal stability of the sample while an excessive amount of UV radiation can reduce the degradation temperature.

polymer science

What problem does this paper attempt to address?

This paper mainly discusses how to improve the performance of polylactic acid (PLA)/polybutylene adipate terephthalate (PBAT) blends by inducing a crosslinking network structure through ultraviolet (UV) irradiation. PLA is a biodegradable polymer, but its inherent rigidity and brittleness limit its applications. In this study, the authors mixed PBAT with PLA to enhance its toughness and flexibility, and further utilized TAIC as a crosslinking agent to induce crosslinking structure through UV irradiation.

The experimental results showed that the addition of PBAT significantly improved the flexibility and elongation at break of PLA, and the crosslinking structure formed by UV irradiation further enhanced the compatibility of these two materials. In particular, the elongation at break and notch impact strength of the sample treated with 30 minutes of UV (ABT-UV30) were 3.9 times and 8.4 times higher than pure PLA, respectively. With the extension of UV irradiation time, the glass transition temperature (Tg) of PLA and the melting point of PBAT gradually increased until they approached consistency. Moderate UV irradiation could improve the thermal stability of the samples, but excessive irradiation would cause a decrease in degradation temperature.

Keywords include: biodegradable, polylactic acid, polybutylene adipate terephthalate, crosslinking structure. The study found that the addition of PBAT and UV-induced crosslinking can effectively solve the brittleness issue of PLA, improve its mechanical properties, and maintain good thermal performance. However, excessive crosslinking may lead to a decrease in material flexibility.