Remarkable Magnetic Exchange Coupling via Constructing Bi‐Magnetic Interface for Broadband Lower‐Frequency Microwave Absorption
Mingyue Yuan,Biao Zhao,Chendi Yang,Ke Pei,Longyuan Wang,Ruixuan Zhang,Wenbin You,Xianhu Liu,Xuefeng Zhang,Renchao Che
DOI: https://doi.org/10.1002/adfm.202203161
IF: 19
2022-06-09
Advanced Functional Materials
Abstract:Easily prepared and uniformly coated core‐shell BaFe(12‐x)CoxO19@Fe3O4 microsphere is fabricated using facile spray‐drying and subsequent solvothermal approach. The unique microsphere intensifies the degree of coupling between the hard/soft magnetic phases, achieves the breakthrough of Snoek's limitation, and triggers improved magnetic loss and a large‐scale magnetic interaction network to reach superior lower‐frequency microwave absorption performance. Severe lower‐frequency (2–8 GHz) microwave pollution caused by the rapid development of 5th generation (5G) communication posts significance on cutting‐edge microwave absorbers. However, the intensely coupled wave‐impedance and microwave dissipating ability dramatically hinder their performance in the exact lower‐frequency range. The rationally designed heterostructure of hard/soft ferrite composite provides an efficient solution to address the issue. In this context, core‐shell structured hard/soft BaFe(12‐x)CoxO19@Fe3O4 with abundant heterointerface is created using facile spray‐drying and subsequent solvothermal approach, where hard magnetic BaFe(12‐x)CoxO19 serves as the core and soft magnetic Fe3O4 serves as the shell, respectively. The unique core‐shell integration contributes sufficient magnetic exchange coupling interaction for strong magnetic loss beyond Snoek's limitation, which considerably boosts a lower‐frequency microwave absorption. Accordingly, the minimum reflection loss (RLmin) of typical BaFe11.6Co0.4O19@Fe3O4 microcomposite reaches −48.9 dB at the thickness of 3.5 mm, its bandwidth of reflection loss
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology