Abstract:The demand for advanced Al-based alloys with tailored structural and magnetic properties has intensified for applications requiring a high thermal stability and performance under challenging conditions. This study investigated the phase evolution, magnetic properties, thermal stability, and microstructural changes in the Al-based alloys Al82Fe16Nb2 and Al82Fe14Nb2Mn2, synthesized via mechanical alloying (MA), using stearic acid as a process control agent. The X-ray diffraction results indicated that Al82Fe16Nb2 achieved a β-phase solid solution with 13–14 nm crystallite sizes after 5 h of milling, reaching an amorphous state after 10 h. In contrast, Al82Fe14Nb2Mn2 formed a partially amorphous structure within 10 h, with enhanced stability with additional milling. Magnetic measurements indicated that both alloys possessed soft magnetic behavior under shorter milling times (1–5 h) and transitioned to hard magnetic behavior as amorphization progressed. This phenomenon was associated with a decrease in saturation magnetization (Ms) and an increase in coercivity (Hc) due to structural disorder and residual stresses. Thermal stability analyses on 10 h milled samples conducted via differential scanning calorimetry showed exothermic peaks between 300 and 800 °C, corresponding to phase transformations upon heating. Post-annealing analyses at 550 °C demonstrated the presence of phases including Al, β-phase solid solutions, Al13Fe4, and residual amorphous regions. At 600 °C, the Al3Nb phase emerged as the β-phase, and the amorphous content decreased, while annealing at 700 °C fully decomposed the amorphous phases into stable crystalline forms. Microstructural analyses demonstrated a consistent reduction in and homogenization of particle sizes, with particles decreasing to 1–3 μm in diameter after 10 h. Altogether, these findings highlight MA's effectiveness in tuning the microstructure and magnetic properties of Al–Fe–Nb (Mn) alloys, making these materials suitable for applications requiring a high thermal stability and tailored magnetic responses.

Enhancement of Coercivity in α-Mn(Al) Magnetic Nanopowders Processed by High-Energy Ball Milling

Nanocrystalline/Amorphous Tuning of Al–Fe–Nb (Mn) Alloy Powders Produced via High-Energy Ball Milling

Structural and Magnetic Properties of Mn50Al46Cu4C3 Flakes Obtained by Surfactant-Assisted Ball Milling

Effect of Milling on the Structure and Magnetic Properties in Mn54Al46 Flakes Prepared by Surfactant-Assisted Ball Milling

Study on properties of MnAlC magnetic powder and bulk

Preparation of Nb3al by High-Energy Ball Milling and Superconductivity

Microstructure and magnetic properties of MnBi powders prepared by various ball milling processes

Anisotropic SmFe10V2 Bulk Magnets with Enhanced Coercivity via Ball Milling Process

High coercivity induced by mechanical milling in cobalt ferrite powders

Preparation of Mnalc Flakes by Surfactant-Assisted Ball-Milling and the Effects of Annealing

Phase transformation and magnetic properties of MnAl powders prepared by elemental-doping and salt-assisted ball milling

Magnetic Anisotropy and Enhanced Remanence in Textured Polycrystalline MnAlCuC-based Flakes

Effect of Heat Treatment and Ball Milling on MnBi Magnetic Materials

τ-MnAl with high coercivity and saturation magnetization

Properties of High-Entropy Fe30Co20Ni20Mn20Al10 Alloy Produced by High-Energy Ball Milling

High Coercivity in Mechanically Milled ThMn12-type Nd–Fe–Mo Nitrides

Study on the Influence of Annealing and Ball Milling on the Magnetic Properties of HDDR Nd-Fe-B Magnetic Powder

Anisotropic Nanocrystalline Mnbi with High Coercivity at High Temperature

Microstructural and magnetic property evolution with different heat-treatment conditions in an alnico alloy

Structure and Properties Evolutions for Hard Magnetic MnAl and MnGa Based Alloys Prepared by Melt Spinning or Mechanical Milling

Ultrahigh saturation magnetization in FeCoB powders with controllable amorphous-nanocrystalline structure via the synergism of deformation and energy injection