Tailoring composites via in situ growth of Co-MOF on V 2 CT x MXene as high-performance anode for lithium-ion batteries

Wu Gong,Shao Qing Li,Fei Gao,Jing Lin,Yong Ye,Xue Rui Yang,Nai Gen Zhou

DOI: https://doi.org/10.1016/j.ssi.2023.116295

IF: 3.699

2023-07-07

Solid State Ionics

Abstract:MXenes, as a new family of 2D materials , have attracted extensive attention for their high electrical conductivity and good electrochemical cycling stability. However, due to the self-stacking nature of MXene materials, the actual specific capacity (260 mAh g −1 ) of V 2 CT x MXene materials as anodes is much lower than the theoretical specific capacity (940 mAh g −1 ). Herein, we designed a novel Co-MOF/V 2 CT x composite (denoted as Co-MOF/V 2 CT x ), where Co-MOF was in situ grown on the surface and interlayer of the V 2 CT x MXene with larger interlayer spacing. The MOF in the composite provides the additional specific capacity as well as effectively prevented the restacking of V 2 CT x MXene, which exposed more Li + active sites. Besides, benefiting from the high conductivity, electrochemical stability, and strong bonding with the Co-MOF at the interface of MXene, the structural stability of Co-MOF itself in composite materials can be better improved. Consequently, the cells with Co-MOF/V 2 CT x anodes realize a high specific capacity of 484.3 mAh g −1 after 120 cycles at 100 mA g −1 and superior cycling stability even at a higher current density of 500 mA g −1 . The unique synergistic design of this work can provide new ideas for the development of MXene-based composites in energy storage applications.

chemistry, physical,physics, condensed matter