Smart Strategy: Transparent Hole-Transporting Polymer as a Regulator to Optimize Photomultiplication-type Polymer Photodetectors
Kaixuan Yang,Jian Wang,Zijin Zhao,Zhengji Zhou,Ming Liu,Jian Zhang,Zhiqun He,Fujun Zhang
DOI: https://doi.org/10.1021/acsami.1c06486
2021-04-28
Abstract:Photomultiplication-type polymer photodetectors (PM-PPDs) were fabricated with hole-only transport active layers containing polymer(s): [6,6]-phenylC61-butyric acid methyl ester (PC<sub>61</sub>BM) with a weight ratio of 100:2. The rather less PC<sub>61</sub>BM content in active layers prefers to generate a large amount of isolated electron traps surrounded by polymers. Photogenerated electrons prefer to be trapped by the isolated PC<sub>61</sub>BM due to the lack of continuous electron-transport channels. The trapped electrons by the isolated PC<sub>61</sub>BM close to the Al electrode would like to seduce hole tunneling injection. The transparent polymer poly[<i>N</i>,<i>N</i>′-bis(4-butylphenyl)-<i>N</i>,<i>N</i>′-bis(phenyl)benzidine] (poly-TPD) was incorporated as a regulator to improve hole mobility (μ<sub>h</sub>) and adjust the trapped-electron distribution in active layers, leading to the enhanced performance of PM-PPDs. The optimal PM-PPDs were achieved using poly(3-hexylthiophene) (P3HT):poly-TPD:PC<sub>61</sub>BM (80:20:2, wt/wt/wt) as active layers. External quantum efficiency (EQE) values at 620 nm are 3900 and 1250% for PM-PPDs based on P3HT:poly-TPD:PC<sub>61</sub>BM (80:20:2, wt/wt/wt) and P3HT:PC<sub>61</sub>BM (100:2, wt/wt) under −10 V applied voltage, respectively. The EQE at 620 nm of optimal PM-PPDs is improved from 650 to 63,000% along with the applied voltage increase from −5 to −20 V. This work provides a new strategy of using transparent polymer with large μ<sub>h</sub> as a regulator for EQE and response speed improvement, as well as the flattened EQE spectral shape of PM-PPDs.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.1c06486?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.1c06486</a>.<i>J–V</i> curves of poly-TPD:PC<sub>61</sub>BM (100:1, wt/wt)-based devices, PL spectra of neat poly-TPD films and poly-TPD:PC<sub>61</sub>BM blend films, ln(<i>Jd</i>3/<i>V</i>2)–(<i>V</i>/<i>d</i>)<sup>1/2</sup> curves, absorption spectra of P3HT:poly-TPD:PC<sub>61</sub>BM blend films with different poly-TPD contents, extinction coefficient and refractive index of P3HT:PC<sub>61</sub>BM (100:2, wt/wt) and P3HT:poly-TPD:PC<sub>61</sub>BM (80:20:2, wt/wt/wt) blend films, optical-field distribution in P3HT:PC<sub>61</sub>BM (100:2, wt/wt) and P3HT:poly-TPD:PC<sub>61</sub>BM (80:20:2, wt/wt/wt)-based PM-PPDs, and NEP spectrum of optimal PM-PPDs (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c06486/suppl_file/am1c06486_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology