Synthesis of flexible, strong, and lightweight oxide ceramic nanofibers via direct electrospinning of inorganic sol for thermal insulation

Cheng Liu,Lin Tang,Yingying Zhang,Pan Jiang,Ni Wang,Xia Yin,Jianyong Yu,Yi-Tao Liu

DOI: https://doi.org/10.1080/00405000.2024.2319358

IF: 1.7698

2024-02-25

Journal of the Textile Institute

Abstract:Oxide ceramic nanofibers are widely used in aerospace and civil facilities due to their superior thermal stability and fire resistance. Currently, electrospinning, one of the important methods for preparing oxide ceramic nanofibers, must rely on adding organic polymers to impart spinnability to inorganic sols. However, these organic polymers will inevitably leave hole flaws in the ceramic nanofibers due to thermal decomposition during the subsequent ceramization process, seriously damaging their mechanical properties. Here, a direct electrospinning strategy for inorganic sol through hydrolyzation–polycondensation rate modulation is proposed, which gets rid of the dependence of spinnability of inorganic sol on organic polymer. Taking silica nanofibers as an example, it exhibits excellent flexibility and mechanical strength (tensile stress up to 1.4 MPa), as well as thermal insulation properties (thermal conductivity as low as 0.0551 W m −1 K −1 at 300 °C). This work provides new insights into developing other high–performance oxide ceramic materials.

materials science, textiles

What problem does this paper attempt to address?

The paper aims to address the issue of relying on organic polymers in the preparation of oxide ceramic nanofibers and proposes a direct electrospinning strategy without the need for organic polymer templates to improve the mechanical and thermal insulation properties of oxide ceramic nanofibers.

Specifically, the current method of electrospinning to prepare oxide ceramic nanofibers requires the addition of organic polymers to impart spinnability. However, during the subsequent high-temperature sintering process, these organic polymers decompose and leave pore defects, severely affecting the mechanical properties of the final product. Therefore, the paper proposes a new method of direct electrospinning of inorganic sols by adjusting the hydrolysis-polycondensation rate, thereby avoiding the introduction of organic polymer templates. Experimental results show that silica nanofibers prepared by this method exhibit excellent flexibility and mechanical strength (tensile stress up to 1.4 MPa), as well as outstanding thermal insulation properties (thermal conductivity as low as 0.0551 W/m·K at 300°C). This research provides a new perspective for the development of other high-performance oxide ceramic materials.