Facile synthesis of a P/N-containing heterocyclic compound for simultaneous enhancement of heat resistance, mechanical properties and fire safety of epoxy resin
Chentao Liu,Huajun Duan,Huijuan Zhao,Yuan Gao,Juan Zhang,Jin Kang,Huiru Ma
DOI: https://doi.org/10.1016/j.reactfunctpolym.2023.105530
IF: 4.966
2023-02-07
Reactive and Functional Polymers
Abstract:The demand for flame retardancy in epoxy thermosetting resins (EP) has become increasingly urgent, but the mechanical properties should not be damaged while ensuring flame-retardancy efficiency. To achieve this, a heterocyclic compound (BDP) containing reactive functional groups was successfully synthesized by 2,4-Diamino-6-phenyl-1,3,5-triazine (DPT), paraformaldehyde and 9, 10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPO) in a one-pot process. From the analysis of the curing behavior, the addition of BDP facilitated the curing reaction of EP by reducing the apparent activation energy (E c ). Dynamic mechanical analysis (DMA) and flexural tests indicated an increase in the glass transition temperature (T g ) and flexural strength of the flame-retardant epoxy resin (FREP) increased by 5.2% and 8.9% respectively, caused by an enhancement of intermolecular forces. As well, a V-0 classification in vertical combustion with a limiting oxygen index (LOI) of 35.2% was attained at a phosphorus content of merely 0.48 wt%. Cone calorimetric (CC) test demonstrated that total smoke production (TSP) and the peak heat release rate (PHRR) of EP-7.5/BDP were reduced by approximately 19.2% and 29.4% respectively in comparison to EP. This positive smoke inhibition and flame retardancy were caused by the blocking and dilution effect presented by the FREP during combustion.
engineering, chemical,chemistry, applied,polymer science