Abstract:The present study focuses on pure and antimony (Sb)-doped tin oxide thin film and its influence on their structural, optical, and electrical properties. Both undoped and Sb-doped SnO2 thin films have been grown by using simple, inexpensive pyrolysis spray technique. The deposition temperature was optimized to 450 °C. X-ray diffractions pattern have revealed that the films are polycrystalline and have tetragonal rutile-type crystal structure. Undoped SnO2 films grow along (110) preferred orientation, while the Sb-doped SnO2 films grow along (200) direction. The size of Sb-doped tin oxide crystals changes from 26.3 to 58.0 nm when dopant concentration is changed from 5 to 25 wt%. The transmission spectra revealed that all the samples are transparent in the visible region, and the optical bandgap varies between 3.92 and 3.98 eV. SEM analysis shows that the surface morphology and grain size are affected by the doping rate. All the films exhibit a high transmittance in the visible region and show a sharp fundamental absorption edge at about 0.38–0.40 nm. The maximum electrical conductivity of 362.5 S/cm was obtained for the film doped with 5 wt% Sb. However, the carrier concentration is increased from 0.708 × 1018 to 4.058 × 1020 cm3. The electrical study reveals that the films have n-type electrical conductivity and depend on Sb concentration. We observed a decrease in sheet resistance and resistivity with the increase in Sb dopant concentration. For the dopant concentration of 5 wt% of Sb in SnO2, the Rs and ρ were found minimum with the values of 88.55 (Ω cm−2) and 2.75 (Ω cm), respectively. We observed an increase in carrier concentration and a decrease in mobility with the addition of Sb up to 25 wt%. The highest figure of merit values 2.5 × 10–3 Ω−1 is obtained for the 5wt% Sb, which may be considered potential materials for solar cells' transparent windows.

Spray pyrolyzed Al-doped SnO2 films with desirable type inversion and physical properties for use in transparent thin-film heater

Transparent P-Type Conducting Indium-Doped SnO2 Thin Films Deposited by Spray Pyrolysis

Al-doped SnO2 thin films as transparent heater: effect of tin (II) chloride concentration

P-type Transparent Conducting Indium-Tin Oxide Thin Films Deposited by Spray-pyrolysis

P-type Tin–indium Oxide Films Prepared by Thermal Oxidation of Metallic InSn Alloy Films

Transparent conductive F-doped SnO 2 films prepared by RF reactive magnetron sputtering at low substrate temperature

Synthesis and Characterization of Al-doped NiO Nanostructured Thin Films Elaborated by Solar Spray Pyrolysis Technique, for Photovoltaic Cells

Influence of Heat Treatment on the Characteristic of SnO2 Thin Films for Gas Sensor Application

Flexible Transparent Heater Fabricated from Spray-Coated In:ZnO/Ag-NWs/In:ZnO Multilayers on Polyimide Foil

Sputtering deposition of transparent conductive F-doped SnO2 (FTO) thin films in hydrogen-containing atmosphere

Influence of Oxygen Flow on Structural, Optical, and Electrical Properties of Al:SnO2 Films Deposited at Room Temperature

Enhanced ultraviolet photodetector based on Al-doped ZnO thin films prepared by spray pyrolysis method

TRANSPARENT CONDUCTIVE SnO2 : Sb THIN FILM PREPARED BY SPRAY PYROLYSIS METHOD

From Transparent Conducting Material to Gas-Sensing Application of SnO2:Sb Thin Films

Characterization and Performance Evaluation of Ni-Doped SnO2 Thin Films for Optoelectronic Applications: Structural, Optical, and Electrical Insights

Flow rate-dependent properties of SnO 2 thin films deposited by ultrasonic spray pyrolysis

UV photo-sensing performance of NiSnO3 thin films deposited by pulsed spray pyrolysis technique

Synthesis and physical investigation of Al doped La2O3 thin films for wettability applications

Preparation of Sb:SnO2 thin films and its effect on opto-electrical properties

Deposition Mechanism and Characterization of Plasma-Enhanced Atomic Layer-Deposited SnOx Films at Different Substrate Temperatures