Ultralow Ru-doped NiMoO4@Ni3(PO4)2 Core-Shell Nanostructures for Improved Overall Water Splitting
Adel Al-Salihy,Ce Liang,Abdulwahab Salah,Abdel-Basit Al-Odayni,Ziang Lu,Mengxin Chen,Qianqian Liu,Ping Xu
DOI: https://doi.org/10.1016/s1872-2067(24)60038-0
IF: 16.5
2024-01-01
Chinese Journal of Catalysis
Abstract:The potential of sustainable hydrogen production technology through water splitting necessitates the rational design of oxygen evolution reaction (OER) and hydrogen evolution reaction (HER) bi-functional electrocatalysts. In this context, we initially synthesized and empirically evaluated ultralow Ru-doped NiMoO4@Ni-3(PO4)(2) core-shell nanostructures on nickel foam (Ru-NiMoO4@Ni-3(PO4)(2)/NF). The hydrous NiMoO 4 nanopillars were hydrothermally grown on NF, followed by successive RuCl 3 etching and subsequent phosphorylation processes, leading to the final Ru-NiMoO4@Ni-3(PO4)(2)/NF. The catalyst demonstrated impressive HER overpotential values of -14.8 and -57.1 mV at 10 and 100 mA cm -2 , respectively, with a Tafel slope of 35.8 mV dec -1 . For OER at 100 mA cm -2 , an overpotential of 259.7 mV was observed, with a Tafel slope of 21.6 mV dec -1 . The cell voltage required for overall water splitting was 1.43 V at 10 mA cm -2 and 1.68 V at 100 mA cm -2 . Moreover, the catalyst exhibited superior stability for 150 h, emphasizing its practical utility for long-term applications. Subsequent density functional theory calculations aligned with these empirical findings, indicating a low water dissociation energy barrier (Delta G b = 0.46 eV), near-zero free adsorption energy for HER (triangle G *H = 0.02 eV), and suitable free adsorption energy for OER (Delta G *OOH - Delta G *OH = 2.74 eV), alongside a high density of states near the Fermi level. These results, informed by both experimental evaluation and theoretical validation, highlight the potential of Ru-NiMoO 4 @Ni 3 (PO 4 ) 2 /NF as a high-performance catalyst for water splitting, setting a solid foundation for advancements in sustainable energy technologies. (c) 2024, Dalian Institute of Chemical Physics, Chinese Academy of Sciences. Published by Elsevier B.V. All rights reserved.