Energy transfer properties of a single-phase Na3Gd(PO4)2: Eu2+, Mn2+ phosphor with excellent thermal stability for w- LEDs

Meiling Xie,Meihua Wu,Minghao Fang,Zhaohui Huang,Xiaowen Wu,Yan-Gai Liu,xin min

DOI: https://doi.org/10.1039/d2dt01439d

IF: 4

2022-08-18

Dalton Transactions

Abstract:The high temperature solid state method was used to prepare Na3Gd(PO4)2: Eu2+, Mn2+ phosphor with good thermal stability. The phosphor has a broadband excitation region of 250-430nm, which can match with the emissions of the ultraviolet (UV)/near-ultraviolet (NUV) LED chips for white light emitting diodes (w-LEDs). The energy transfer efficiency is 74.46 % from the sensitizer Eu2+ ions to the activator Mn2+ ions, which enhances the intensities of Na3Gd(PO4)2-based phosphor. In addition, by increasing the Mn2+ doping level in the phosphor, the Na3Gd(PO4)2: Eu2+, Mn2+ phosphor show first shows blue light, then turns to white light, and finally emits red light under the 365nm excitation. Besides, the temperature-dependent photoluminescence measurements indicate that the prepared phosphors exhibit good thermal stability. W-LEDs fabricated by combining a 365 nm chip with the Na3Gd(PO4)2: Eu2+, Mn2+ phosphor exhibit bright white light,which has high color rendering index (CRI)=91.5, and relatively low correlated color temperature (CCT)=5198K. Moreover, the CIE point is calculated to be at (0.3337, 0.3465), locating in the white light region. These results indicate that the as-prepared phosphors can be considered as potential candidates for UV/NUV light-excited w-LEDs applications.

chemistry, inorganic & nuclear