Comparative biopolymeric assessment of paddy straw during thermal degradation process

Mattaparthi Lakshmi Durga,Sandip Gangil
DOI: https://doi.org/10.1016/j.jaap.2024.106556
IF: 6
2024-05-24
Journal of Analytical and Applied Pyrolysis
Abstract:This article presents a novel process that can be employed on rice straw to obtain carbon and lignin enriched biomaterial. Use of acceleration and retardation thermal behaviour for comparative investigation was presented first time for rice straw, in this writing. In the present study, carbonization was done at 350, 400 and 450°C for 15, 30 and 45 min. Thenceforth, the char samples under the pre-mentioned conditions were subjected to surface area measurements. The highest surface area carbonized paddy straw was selected for thermo gravimetric analysis (TGA) analysis and other surface morphological analyses. Highest surface area as 47.46 m 2 /g and pore volume as 0.07 cc/g was obtained at 400 °C and 45 min. Carbonization process enhanced carbon by 1.9 times, lignin by 1.9 times and adsorbance by 3.8 time in carbonized as compared to raw paddy straw. To elaborate the mechanisms of each biopolymer individually in raw and carbonized samples, multi-step mechanism was employed. The average activation energy of raw paddy straw was higher than the carbonized char, because of the devolatilization of hemicellulose during carbonization. The activation energies of raw paddy straw were 212, 167.27 and 215.2 kJ/mol for cellulose, lignin and hemicellulose, respectively. Thermal degradation reduced the activation energy drastically as 23.34 and 12.95 kJ/mol for cellulose and lignin, respectively. Critically, the degradation behaviour of raw and carbonized char was found in-line with the trend of the diffusion (D) model (regardless of the order of reaction).
engineering, chemical,chemistry, analytical,energy & fuels
What problem does this paper attempt to address?