Abstract:The past decade has seen tremendous progress in the synthesis and surface functionalization of iron oxide nanoparticles (IONPs) for a variety of biomedical applications. However, there is still a growing demand on magnetic nanoparticles with higher magnetic moments for more sensitive diagnosis and lower dose treatments in magnetic bioassays, imaging, and therapies. In view of this need, the γ′-Fe4N nanoparticle, with around 3 times higher saturation magnetizations than IONPs, becomes one promising alternative for these applications. However, the large and non-uniformly distributed sizes of γ′-Fe4N nanoparticles hinder the biomedical applications. These synthesized γ′-Fe4N nanoparticles are not suitable for biomedical applications at the current stage. Herein, we have developed and demonstrated a wet ball milling method along with different surface-active media to produce ultrastable, monodispersed, uniformly sized, and sub-100 nm γ′-Fe4N nanoparticles in solvents. Different standard characterization methods such as transmission electron microscopy, nanoparticle tracking analysis, and Fourier-transform infrared spectroscopy are carried out to measure the physicochemical properties of these surface-functionalized γ′-Fe4N nanoparticles. It is confirmed that the functional chemical groups have been successfully anchored on our purified sub-100 nm γ′-Fe4N nanoparticles, which allows for convenient subsequent conjugation of proteins, nucleic acids, and drugs for future in vitro and in vivo biomedical applications.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsanm.0c03421?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsanm.0c03421</a>.Photographs of γ′-Fe4N nanoparticle colloidal suspensions; magnetic core size distributions of samples (X = A, B, and D) from TEM images; and hydrodynamic size distributions and percentile size distributions of samples (X = A, B, C, and D) (<a class="ext-link" href="/doi/suppl/10.1021/acsanm.0c03421/suppl_file/an0c03421_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

What problem does this paper attempt to address?

The main problem that this paper attempts to solve is to develop a synthesis and surface functionalization strategy to obtain a suspension of γ′-Fe₄N nanoparticles that are ultras table, monodisperse, uniform in size and less than 100 nm for magnetic diagnosis and treatment. Specifically, the research aims to: 1. **Improve magnetic properties**: The saturation magnetization of γ′-Fe₄N nanoparticles is approximately three times that of iron oxide nanoparticles (IONPs), so it has higher sensitivity and lower dose requirements in magnetic bioassays, imaging and treatment. 2. **Solve existing problems**: Currently, the synthesized γ′-Fe₄N nanoparticles are large in size and unevenly distributed, which limits their use in biomedical applications. The paper solves this problem through wet ball milling and different surface - active media to obtain nanoparticles with smaller size and narrower distribution. 3. **Achieve surface functionalization**: Through surface functionalization, γ′-Fe₄N nanoparticles can be conveniently combined with proteins, nucleic acids and drugs, so as to carry out in - vitro and in - vivo biomedical applications in the future. ### Main content of the paper 1. **Background introduction**: - In the past decade, iron oxide nanoparticles (IONPs) have made remarkable progress in a variety of biomedical applications, but the demand for high - magnetic - moment nanoparticles is still growing. - γ′-Fe₄N nanoparticles have become promising alternative materials because of their high saturation magnetization (approximately three times that of IONPs). - However, the existing γ′-Fe₄N nanoparticles are large in size and unevenly distributed, and are not suitable for biomedical applications. 2. **Experimental methods**: - **Synthesis of γ′-Fe₄N nanoparticles**: The gas nitriding method is adopted. First, γ - Fe₂O₃ nanoparticles are reduced to Fe nanoparticles, and then nitrided in a mixed atmosphere of ammonia and hydrogen. - **Surface functionalization**: Surface functionalization is carried out through wet ball milling and four different surface - active media (water, commercial nanoparticle surfactant, oleic acid, tetramethylammonium hydroxide solution). - **Characterization methods**: Standard methods such as transmission electron microscopy (TEM), nanoparticle tracking analysis (NTA), and Fourier transform infrared spectroscopy (FTIR) are used to characterize the physicochemical properties of nanoparticles. 3. **Results and discussion**: - **Magnetic properties**: The saturation magnetization of the synthesized γ′-Fe₄N nanoparticles is significantly higher than that of γ - Fe₂O₃ nanoparticles. - **Morphology and size**: Through TEM and NTA measurements, it is found that the γ′-Fe₄N nanoparticles treated with commercial surfactant and tetramethylammonium hydroxide are small in size and uniformly distributed. - **Colloidal stability**: Through ζ - potential analysis and a 21 - day observation period, it is confirmed that the γ′-Fe₄N nanoparticles treated with commercial surfactant and tetramethylammonium hydroxide have good colloidal stability. - **Surface chemical groups**: Through FTIR spectral analysis, it is confirmed that the surface - active groups have been successfully anchored on the surface of γ′-Fe₄N nanoparticles. ### Conclusion This research has successfully developed a synthesis and surface functionalization strategy and prepared a suspension of γ′-Fe₄N nanoparticles that are ultras table, monodisperse, uniform in size and less than 100 nm, providing new possibilities for magnetic diagnosis and treatment.

Stable and Monodisperse Iron Nitride Nanoparticle Suspension for Magnetic Diagnosis and Treatment: Development of Synthesis and Surface Functionalization Strategies