A Rapid Thermal Absorption Rate and High Latent Heat Enthalpy Phase Change Fiber Derived from Bio-Based Low Melting Point Copolyesters

Tsung-Yu Lan,Hsu-I Mao,Chin-Wen Chen,Yi-Ting Lee,Zhi-Yu Yang,Jian-Liang Luo,Pin-Rong Li,Syang-Peng Rwei
DOI: https://doi.org/10.3390/polym14163298
IF: 5
2022-08-13
Polymers
Abstract:A series of poly(butylene adipate-co-hexamethylene adipate) (PBHA) copolymers with different content of 1,4-cyclohexanedimethanol (CHDM) was synthesized via one-step melt polymerization. The PBHA copolymer with 5 mol% CHDM (PBHA-C5) exhibited a low melting point (Tm) and high enthalpy of fusion (∆Hm) of 35.7 °C and 43.9 J g−1, respectively, making it a potential candidate for an ambient temperature adjustment textile phase change material (PCM). Polybutylene terephthalate (PBT) was selected as the matrix and blended at different weight ratios of PBHA-C5, and the blended samples showed comparable Tm and ∆Hm after three cycles of cooling and reheating, indicating good maintenance of their phase changing ability. Samples were then processed via melt spinning with a take-up speed of 200 m min−1 at draw ratios (DR) of 1.0 to 3.0 at 50 °C. The fiber's mechanical strength could be enhanced to 2.35 g den−1 by increasing the DR and lowering the PBHA-C5 content. Infrared thermography showed that a significant difference of more than 5 °C between PBT and other samples was achieved within 1 min of heating, indicating the ability of PBHA-C5 to adjust the temperature. After heating for 30 min, the temperatures of neat PBT, blended samples with 27, 30, and 33 wt% PBHA-C5, and neat PBHA-C5 were 53.8, 50.2, 48.3, 47.2, and 46.5 °C, respectively, and reached an equilibrium state, confirming the temperature adjustment ability of PBHA-C5 and suggesting that it can be utilized in thermoregulating applications.
polymer science
What problem does this paper attempt to address?
This paper aims to solve the problem of developing a phase - change material (PCM) fiber with fast heat absorption rate and high latent heat enthalpy, which is derived from bio - based low - melting - point copolyester. Specifically, the research attempts to solve the problem in the following ways: 1. **Synthesize copolymers with specific properties**: Poly(butylene succinate - co - hexylene adipate) (PBHA) copolymers containing different contents of 1,4 - cyclohexanedimethanol (CHDM) were synthesized by a one - step melt polymerization method. These copolymers have a lower melting point and a higher melting enthalpy, making them potential phase - change materials for room - temperature - regulating textiles. 2. **Improve the thermal energy storage capacity of fibers**: Polybutylene terephthalate (PBT) was selected as the matrix and mixed with PBHA - C5 (PBHA copolymer containing 5 mol% CHDM) at different weight ratios. The mixed samples maintained similar melting points and melting enthalpies after three cooling and reheating cycles, indicating their good phase - change ability. 3. **Optimize the mechanical properties and thermal regulation ability of fibers**: Fibers were prepared by the melt - spinning process, and the effects of different draw ratios and PBHA - C5 contents on the mechanical properties of the fibers were studied. The results showed that increasing the draw ratio and decreasing the PBHA - C5 content could enhance the mechanical strength of the fibers. In addition, infrared thermal imaging showed that there was a significant temperature difference of more than 5 °C between PBT and other samples after heating for 1 minute, confirming the temperature - regulation ability of PBHA - C5. In summary, this research aims to develop an intelligent temperature - regulating textile that can undergo phase change near the human body surface temperature, thereby improving the functionality and comfort of textiles. By introducing an appropriate amount of CHDM, not only can the melting viscosity of the copolymer be improved and leakage prevented, but also good thermal energy storage and release characteristics can be maintained, which are suitable for temperature - control applications. ### Formula summary - Melting point ($T_m$) and melting enthalpy ($\Delta H_m$): - The melting point of PBHA - C5 is $T_m = 35.7^{\circ}\text{C}$, and the melting enthalpy is $\Delta H_m = 43.9 \, \text{J/g}$. - Crystallization temperature ($T_c$) and crystallization enthalpy ($\Delta H_c$): - During the first cooling process, the crystallization temperature decreased from 19.5 °C to 16.1 °C, and the crystallization enthalpy decreased from 49.5 J/g to 45.2 J/g. - Glass transition temperature ($T_g$): - As the CHDM content increased, the glass transition temperature gradually increased from - 58.9 °C to - 52.4 °C. These parameter changes reflect the influence of the introduction of CHDM on the structure and properties of the copolymer.