Controlled hydrothermal synthesis of Prussian Blue films with multicolor electrochromic behaviors

Mingqing Yang,Zhiyuan Liu,Xiaoying Li,Yanlin Wang,Chunhui Niu,Yong Lv

DOI: https://doi.org/10.1016/j.jssc.2023.124160

IF: 3.3

2023-09-01

Journal of Solid State Chemistry

Abstract:Prussian blue films were fabricated on fluorine doped tin dioxide glass by a hydrothermal technique through modulation of reactants, reaction temperature and reaction duration. Reagents and hydrothermal temperature were found to largely affect the color, structure, and property of PB films. When the dosage of hydrobromic acid was above 0.9 mL and the hydrothermal temperature was above 120 °C, the reagents could react completely. A plausible formation mechanism of PB was proposed based on experimental results. Hydrobromic acid acts as both a reducing agent and a strong acid in the hydrothermal process. The PB film obtained in presence of 0.9 mL HBr by a hydrothermal treatment at 180 °C for 1h shows a good cycle stability. The PB devices with “sandwich” structure were assembled and exhibited multicolor electrochromic behaviors, and could change the color from initial blue to transparent and green, reversibly, under different power supplies. The coloration efficiency values of PB device were ca. 50.1 and 27.6 cm2/C, corresponding to the process from PB to PW and PG, respectively.

chemistry, physical, inorganic & nuclear