Enhancement of low temperature crack resistance of warm mix asphalt with plastic waste derived additive synthesised by co-pyrolysis method

Hüseyin Köse,Osman Nuri Çelik
DOI: https://doi.org/10.1080/10298436.2024.2431603
2024-11-30
International Journal of Pavement Engineering
Abstract:This study investigated the effect of char (C) and wax (W) products obtained by co-pyrolysis of polyethylene terephthalate (PET) and high-density polyethylene (PE) type waste plastics on the low temperature performance of warm mix asphalt (WMA). PETPE-modified bitumen were prepared by adding various dosages of co-pyrolytic char/wax to virgin bitumen. Sasobit® was preferred as the reference WMA additive. Bending Beam Rheometer test results indicated that bitumen exhibited more flexible behaviour at low temperature with the addition of PETPE-C(6%)-W(6%). Thermal Stress Restrained Specimen Test results showed that WMA-P (PETPE-C(6%)-W(6%)) fractured at 3.10°C lower than hot mix asphalt (HMA) and 4.01°C lower than WMA-S (Sasobit® 3%), respectively. On the other hand, fracture stress of WMA-P was found to be 28% and 4.5% higher than HMA and WMA-S, respectively. Furthermore, Dynamic Shear Rheometer, Marshall stability and Hamburg Wheel Tracking test results demonstrated that the addition of PETPE-C(6%)-W(6%) did not compromise the high temperature performance of bitumen and asphalt mixture. Based on the economic analysis, pyrolytic additive cost was 0.68 $/kg, which equalised the production costs of WMA-P and HMA. WMA-S was also produced at a 4.4% higher cost than HMA. Consequently, PETPE-C(6%)-W(6%) has an improving effect on the low temperature performance of WMA.
construction & building technology,engineering, civil,materials science, characterization & testing
What problem does this paper attempt to address?