Abstract:Three-dimensional (3D) porous nanomaterials with large surface area and abundant surface defects have promising potential in gas sensing due to the following merits: (i) large contact area of gaseous species with the materials, and more adsorption sites on the highly defective surface, (ii) good accessibility to gaseous species of the 3D open structure, (iii) fast electron transport among the 3D network. Rational design and controlled synthesis of the 3D porous nanomaterials with specific morphology and microstructure are essential for improving the performance of gas sensing. In this work, 3D ZnO porous microflowers were prepared by directly calcining the zinc-based flowerlike precursor at 400 degrees C in air. The precursor was preformed through a simple coprecipitation method, i.e., by refluxing the aqueous solution of zinc nitrate and co-precipitators of hexamethylenetetramine and oxalic acid at 90 degrees C for 4 h. The unique ZnO porous microflowers were composed of porous nanosheets of 10 similar to 50 nanometers in thickness and 1 similar to 2 micrometers in width, which inherited from the zinc-based precursor except for the randomly distributed pores on the nanosheet "petals". The 3D porous microstructures endowed ZnO with large specific surface area of 31.3 m(2).g(-1) and abundant surface defects. ZnO porous microflowers were used as active materials to fabricate gas sensors, which exhibited low working temperature, high sensitivity and fast response (recovery) characteristic against ethanol vapor, at the advanced level in comparison with the reported ZnO-based gas sensors for ethanol. The superior performance of the gas sensors could be attributed to the unique microstructures of the ZnO porous nanomaterials. In addition, the sensitivity of the gas sensors showed an exponential relationship with the concentration of ethanol vapor, indicating their capability of quantitative detection within the ethanol volume ratio of 1 X 10(-6)similar to 500 X 10(-6). Together with the superb sensing performance, simple preparation processing and low cost, ZnO porous microflowers have promising application prospect in gas sensing area.

Preparation of hollow bidirectional porous 3D peony-flower structure ZnCO 3 /ZnO with gas sensitive properties at room temperature

Preparation of Hollow Bidirectional Porous 3D Peony-Flower Structure ZnCO3/ZnO with Gas Sensitive Properties at Room Temperature

Synthesis and Gas-Sensing Properties of Zno Porous Microflowers

Polyoxometalates/metal-organic Frameworks-Derived ZnO/ZnWO4 Nanoparticles for Highly Sensitive and Selective Ppb-Level NO2 Detection

Porous ZnO/ZnCo2O4 Hollow Spheres: Synthesis, Characterization, and Applications in Gas Sensing

High Performance Gas Sensors Based on In-Situ Fabricated ZnO/polyaniline Nanocomposite: the Effect of Morphology on the Sensing Properties

Preparation of near room temperature gas sensor based on regular octahedral porous ZnO/SnO2 composite

Preparation of porous Co3O4-ZnO nanosheet composites and study of their gas-sensitive properties

Controllable synthesis of porous 3D Pd loaded ZIF-67/g-C3N4 hierarchical nanostructure for efficient detection of NO2 gas at room temperature

Preparation and gas-sensitive properties of hollow Zn2SnO4/SnO2 nano-cubes

Synthesis and gas sensor properties of flower-like 3D ZnO microstructures

Constructing 2D Porous ZnO Gas Sensors Based on Polyvinylpyrrolidone-Assisted Zn-MOF Nanosheets for NO2 Detection

Facile Non-Template Synthesis Mesoporous Hollow Sphere Zinc Oxide for High Gas Sensitive Ethanol Detection

Multilayered ZnO Nanosheets with 3D Porous Architectures: Synthesis and Gas Sensing Application

ZnO Hollow Spheres: Preparation, Characterization, and Gas Sensing Properties

Porous and Single-Crystalline ZnO Nanobelts: Fabrication with Annealing Precursor Nanobelts, and Gas-Sensing and Optoelectronic Performance

Large-scale synthesis of flowerlike ZnO nanostructure by a simple chemical solution route and its gas-sensing property

Pompon-like Ni doped ZnO mesoporous microspheres for conductometric NO 2 sensing properties at room temperature

Hierarchically Porous Zno Derived from Zeolitic Imidazolate Frameworks for High-Sensitive Mems No2 Sensor

Tunable NH4F-Assisted Synthesis of 3D Porous In2O3 Microcubes for Outstanding NO2 Gas-Sensing Performance: Fast Equilibrium at High Temperature and Resistant to Humidity at Room Temperature.

g-C3N4 templated synthesis of 3DOM SnO2/CN enriched with oxygen vacancies for superior NO2 gas sensing