Influence of water vapour pressure on the carbonation process of calcium monosulfoaluminate 12-hydrate

Dovile Rubinaite,Tadas Dambrauskas,Kestutis Baltakys,Raimundas Siauciunas

DOI: https://doi.org/10.1007/s10973-024-13233-1

IF: 4.755

2024-05-29

Journal of Thermal Analysis and Calorimetry

Abstract:This study aimed to enhance knowledge about the water vapour pressure ( p / p 0 ) impact on the carbonation behaviour of calcium monosulfoaluminate 12-hydrate. The synthesis of monosulfoaluminate was performed by combining mechanochemical treatment (dry grinding at 900 rpm with three on–off cycles of 10 min) and hydrothermal synthesis (for 8 h at 130 °C). The change in mineral composition and carbonation degree of the prepared sample was examined under five different water vapour pressure conditions (varying from 0.355 to 1.0) in the presence of the room CO 2 concentration (668 ± 4 ppm) for up to 90 days. The examination proved that at 0.355 p / p 0 , the sample is the most resistant against carbonation, consuming little monosulfoaluminate after 90 days. Meanwhile, the increase in moisture accelerates the carbonation rate. The detected final carbonation products in all conditions include calcium carbonate, aluminium hydroxide and calcium sulphate hydrate (if ≤ 0.565 p / p 0 —hemihydrate; if ≥ 0.565 p / p 0 —gypsum). At sufficient moisture (≥ 0.753 p / p 0 ), it is observed that Ms12 also converts to ettringite, where crystallization favours within the higher p / p 0 . Additionally, it is successfully observed that water vapour pressure conditions determine the formation of intermediate carbonation products.

chemistry, physical, analytical,thermodynamics