Self-Healing Solid Polymer Electrolyte for Room-Temperature Solid-State Lithium Metal Batteries

Lanshuang Zhang,Panpan Zhang,Caiyun Chang,Wenbin Guo,Zi Hao Guo,Xiong Pu

DOI: https://doi.org/10.1021/acsami.1c14462

2021-09-21

Abstract:Poor room-temperature ionic conductivities and narrow electrochemical stable windows severely hinder the application of conventional poly(ethylene oxide)-based (PEO-based) solid polymer electrolytes (SPEs) for high-energy-density lithium metal batteries (LMBs). Herein, we designed and synthesized a PEO-based self-healing solid polymer electrolyte (SHSPE) via dynamically cross-linked imine bonds for safe, flexible solid LMBs. The constructed dynamic networks endow this SPE with fascinating intrinsic self-healing ability and excellent mechanical properties (extensibility > 500% and stress >130 kPa). More importantly, this SHSPE exhibits ultrahigh ionic conductivity (7.48 × 10–4 S cm–1 at 25 °C) and wide ESW (5.0 V vs Li/Li+). As a result, Li||Li symmetrical cells with the SHSPE showed reliable stability in a >1200 h cycling test under room temperature. The assembled Li|SHSPE|LiFePO4 cell maintained a discharge capacity of 126.4 mAh g–1 after 300 cycles (0.1C, 27 °C). This work highlights a promising strategy for next-generation room-temperature solid-state LMBs.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsami.1c14462.1st cycle charge/discharge curves of the Li|SHSPE|LiFePO4 cell at 0.1C, 0.2C, and 0.5C with a voltage range of 2.5–3.8 V (Figure S1); digital photograph of the thickness of the SHSPE (Figure S2); 90° cross-sectional SEM images (Figure S3); SEM image and EDS mapping analysis of C, Li, and F elements for the SHSPE (Figure S4); TGA of the SHSPE (Figure S5); EIS plots of stainless steel|SHSPE|stainless steel with various temperatures (Figure S6); comparison of the ionic conductivity and stretchability of the SHSPE to other polymer electrolytes reported in the literature (Figure S7); photograph showing the SHSPE under a hanging weight of 20 g (Figure S8); photo image of the SHSPE attached to a glass surface to support 20 g of counterweight (Figure S9); peeling test of the SHSPE (Figure S10); illustration of the coin cell (Figure S11); EIS spectra and the equivalent fitting circuit (inset) of the Li|SHSPE|LiFePO4 cell at 0th (Figure S12); photographs of the Li|SHSPE| LiFePO4 pouch cell to power a calculator and a pedometer (Figure S13) (PDF)This article has not yet been cited by other publications.

materials science, multidisciplinary,nanoscience & nanotechnology