A type of multifunctional cellulose nanocrystal composite silicone-based polymer coating for marine antibiofouling
Jiawen Sun,Xingda Liu,Jizhou Duan,Kunyan Sui,Xiaofan Zhai,Xia Zhao,Yuqing Zhu,Ding Guo,Baorong Hou
DOI: https://doi.org/10.1016/j.ijbiomac.2024.134885
IF: 8.2
2024-08-23
International Journal of Biological Macromolecules
Abstract:Nanocomposite polymer coatings are being used as a new generation of marine antibiofouling coatings because of their toxin-free chemical composition and ease of large-scale adoption. Cellulose nanocrystal (CN) exhibits significant potential for composite reinforcement. Herein, CN was surface-modified via α,ω-bis(3-(2-hydroxyl-terminated polydimethylsiloxane (HTPDMS), resulting in dihydroxyl-terminated poly(dimethylsiloxane)-grafted CN (HP-g-CN). The amine-terminated PDMS as the foundational component was sequentially reacted with isophorone diisocyanate, isophthalaldehyde, and carbon disulfide to produce PDMS-based poly (urea-thiourea-imine) (PDMS-PUTI). Subsequently, a composite (PDMS-PUTI/HP-g-CN) was produced through physical blending. The intrinsic imine bonds and dynamic hydrogen-bonding network were responsible for the self-healing properties, which achieved a healing efficiency of up to 89.2 %. HP-g-CN was grafted with the non-leaching lubricant, HTPDMS, resulting in improved mechanical properties (1.38 MPa of ultimate strength) and adhesion strength (2.43 MPa), along with the self-cleaning and self-lubricating performance (0.700 coefficient) of the coating. Additionally, the fouling resistance to bovine serum albumin (BSA, 10.44 μg cm −2 ), bacteria (∼97.08 % and ∼ 98.05 % reduction for Pseudomonas sp. ( P. sp.) and Shewanella sp. ( S. sp.), respectively), and diatoms (∼27 cells mm −2 ) was further enhanced. Marine field tests conducted over 90 days revealed that the coatings were static fouling-resistant for an extended period. This study demonstrated a multifunctional, high-performance, and environmentally friendly nanocomposite polymer coating for preventing marine biofouling.
polymer science,biochemistry & molecular biology,chemistry, applied