Enhanced thermoelectric performance in Ti(Fe, Co, Ni)Sb pseudo-ternary Half-Heusler alloys
Qingmei Wang,Xiaodong Xie,Shan Li,Zongwei Zhang,Xiaofang Li,Honghao Yao,Chen Chen,Feng Cao,Jiehe Sui,Xingjun Liu,Qian Zhang
DOI: https://doi.org/10.1016/j.jmat.2020.12.015
IF: 8.589
2021-07-01
Journal of Materiomics
Abstract:Ti(Fe, Co, Ni)Sb-based half-Heusler alloys were synthesized by levitation melting, ball milling and SPS.The carrier concentration and the density of states effective mass were significantly increased by Co doping.The lattice thermal conductivity was decreased due to the point defect scattering induced by Hf alloying.●Peak <em>ZT</em>s of ∼0.65 and ∼0.85 at 973 K were achieved in n-type and p-type Ti(Fe, Co, Ni)Sb-based materials, respectively.TiFe<sub>0.5</sub>Ni<sub>0.5</sub>Sb-based half-Heusler compounds have the intrinsic low lattice thermal conductivity and the adjustable band structure. Inspired by the previously reports to achieve both p- and n-type components by tuning the ratio of Fe and Ni based on the same parent TiFe<sub>0.5</sub>Ni<sub>0.5</sub>Sb, we selected Co as the amphoteric dopants to prepare both n-type and p-type pseudo-ternary Ti(Fe, Co, Ni)Sb-based half-Heusler alloys. The carrier concentration, as well as the density of states effective mass was significantly increased by Co doping, contributing to the enhanced power factor of 1.80 mW m<sup>-1</sup> K<sup>-2</sup> for n-type TiFe<sub>0.3</sub>Co<sub>0.2</sub>Ni<sub>0.5</sub>Sb and 2.21 mW m<sup>-1</sup> K<sup>-2</sup> for p-type TiFe<sub>0.5</sub>Co<sub>0.15</sub>Ni<sub>0.35</sub>Sb at 973 K. Combined with the further decreased lattice thermal conductivity due to the strain field and mass fluctuation scattering induced by alloying Hf on the Ti site, peak <em>ZTs</em> of 0.65 in n-type Ti<sub>0.8</sub>Hf<sub>0.2</sub>Fe<sub>0.3</sub>Co<sub>0.2</sub>Ni<sub>0.5</sub>Sb and 0.85 in p-type Ti<sub>0.8</sub>Hf<sub>0.2</sub>Fe<sub>0.5</sub>Co<sub>0.15</sub>Ni<sub>0.35</sub>Sb were achieved at 973 K, which is of great significance for the thermoelectric power generation applications.<span class="display"><span><ol class="links-for-figure"><li><a class="anchor download-link u-font-sans" href="https://ars.els-cdn.com/content/image/1-s2.0-S2352847820305396-fx1_lrg.jpg"><span class="anchor-text">Download : <span class="download-link-title">Download high-res image (316KB)</span></span></a></li><li><a class="anchor download-link u-font-sans" href="https://ars.els-cdn.com/content/image/1-s2.0-S2352847820305396-fx1.jpg"><span class="anchor-text">Download : <span class="download-link-title">Download full-size image</span></span></a></li></ol></span></span>
materials science, multidisciplinary,chemistry, physical,physics, applied