Regulating interfacial reaction through electrolyte chemistry enables gradient interphase for low-temperature zinc metal batteries

Wei Wang,Shan Chen,Xuelong Liao,Rong Huang,Fengmei Wang,Jialei Chen,Yaxin Wang,Fei Wang,Huan Wang

DOI: https://doi.org/10.1038/s41467-023-41276-9

IF: 16.6

2023-09-06

Nature Communications

Abstract:Abstract In situ formation of a stable interphase layer on zinc surface is an effective solution to suppress dendrite growth. However, the fast transport of bivalent Zn-ions within the solid interlayer remains very challenging. Herein, we engineer the SEI components and enable superior kinetics of Zn metal batteries under harsh conditions through regulating the sequence of interfacial chemical reaction. With the differences in chemical reactivity of trimethyl phosphate co-solvent and trifluoromethanesulfonate anions in the Zn 2+ -solvation shell, Zn 3 (PO 4 ) 2 and ZnF 2 are successively generated on Zn metal surface to form a gradient ZnF 2 –Zn 3 (PO 4 ) 2 interphase. Mechanistic studies reveal the outer ZnF 2 facilitates Zn 2+ desolvation and inner Zn 3 (PO 4 ) 2 serves as channels for fast Zn 2+ transport, contributing to long-term cycling at subzero temperatures. Impressively, the gradient SEI enables a high lifespan over 7000 hours in Zn symmetric cell and a capacity retention of 86.1% after 12000 cycles in Zn–KVOH full cell at –50 °C.

multidisciplinary sciences

What problem does this paper attempt to address?

The problem that this paper attempts to solve is the performance degradation of zinc - metal batteries (ZMBs) under low - temperature conditions, especially the performance degradation caused by the solidification of water in the electrolyte at low temperatures and the instability of the solid - electrolyte - interface (SEI) layer. Specifically, the paper focuses on how to form a stable gradient SEI layer by adjusting the electrolyte chemistry to suppress the growth of zinc dendrites, improve the desolvation and transport kinetics of zinc ions at low temperatures, and thus achieve long - term stable cycling of zinc - metal batteries under low - temperature conditions.

### Specific problems solved by the paper include:

1. **Solidification of water**:
- At low temperatures, water molecules in the electrolyte will form ice crystals, causing the electrolyte to solidify and affecting the normal operation of the battery.
- By introducing trimethyl phosphate (TMP) as a co - solvent, the hydrogen bonds between water molecules are broken, the freezing point of the electrolyte is lowered, and its solidification at low temperatures is prevented.

2. **Instability of the SEI layer**:
- The SEI layer formed on the zinc - metal surface is unstable at low temperatures and is prone to cause the growth of zinc dendrites, affecting the cycle life of the battery.
- By regulating the electrolyte components, a gradient SEI layer is formed, with ZnF₂ on the outer layer and Zn₃(PO₄)₂ on the inner layer. ZnF₂ promotes the desolvation of zinc ions, while Zn₃(PO₄)₂ provides a fast zinc - ion transport channel, jointly improving the stability of the SEI layer and the kinetics of zinc ions.

3. **Growth of zinc dendrites**:
- The disordered growth of zinc dendrites will cause internal short - circuits in the battery, seriously affecting the cycle life of the battery.
- The formation of the gradient SEI layer can effectively suppress the growth of zinc dendrites and ensure the uniform deposition of zinc - metal on the electrode surface.

4. **Desolvation and transport of zinc ions**:
- At low temperatures, the desolvation and transport kinetics of zinc ions are significantly slowed down, resulting in a decline in battery performance.
- By optimizing the electrolyte components, the desolvation energy barrier of zinc ions is reduced, and a fast transport channel is provided to improve the transport efficiency of zinc ions at low temperatures.

### Main contributions of the paper:

- **Optimization of electrolyte formula**: By introducing TMP as a co - solvent, a mixed electrolyte with a low freezing point and high ionic conductivity is prepared, which is suitable for low - temperature environments.
- **Formation of gradient SEI layer**: By regulating the electrolyte components, a gradient SEI layer composed of ZnF₂ and Zn₃(PO₄)₂ is formed, which significantly improves the cycling stability and performance of zinc - metal batteries at low temperatures.
- **Experimental verification**: Through electrochemical tests and characterization techniques, the effectiveness and superior performance of the gradient SEI layer are verified, showing its potential in practical applications.

In summary, through systematic research and optimization of electrolyte chemistry, this paper successfully solves the key problems faced by zinc - metal batteries under low - temperature conditions, providing important theoretical and technical support for the development of high - performance low - temperature zinc - metal batteries.