Abstract:Zirconium alloys are important structural materials in nuclear applications. The fuel elements are contained in cladding tubes and are water-cooled. During service the Zircaloy-4 cladding absorbs hydrogen continuously as a result of the metalwater reaction, Zr + 2H20 ~ ZrO2 + 4H. Zirconium hydrides ]precipitate out when the hydrogen concentration is greater than the terminal solubility. The embrittling effect of zirconium hydride in zirconium and its alloys has been known well for many years and has been the topic of much research [1-31. During hydride formation the anisotropic misfit strains between the hydrides and the hexagonalclose-packed (h c p) zirconium matrix results in a preferred orientation of the hydride platelets in the anisotropic stress field caused by non-relieved fabrication residual stresses and misfit stresses, under the influence of microstructure and texture. To understand the mechanism of rupture and to predict the threshold stresses for hydride stress orientation, it is necessary first to study the residual stresses, especially the microstrain caused by crystalline lattice misfit, in a hydrided specimen [3, 4]. An indirect method for estimating these stresses is to correlate the X-ray-measured microstrains in a hydrided specimen with those in a known plastically deformed specimen. The broadened diffraction peak profile characterizes the microstrains and microstresses, which can be related directly to the microstructural modification induced by hydride precipitation or mechanical deformation. In general, the hydride precipitation creates a great number of dislocations, which contributes particularly to the reduction in the coherent domain size and to the increase in microstrain. In this way we can determine the relationship between the hydriding effect and mechanical stressing by microstrain equivalence. In other words, the internal microstrain due to the hydride precipitation effect in hydrided specimens can be calibrated by X-ray diffraction (XRD) profile analysis. This letter gives a detailed description of the equivalence in microstructural evolution between hydriding and plastic deformation in recrystallized Zircaloy-4 based on the results of XRD profile analysis and modelling. Readers are referred to an earlier paper [4] for a more complete background. The material studied was a 0.5 ram-thick sheet of h cp a-phase Zircaloy-4 and the hydrogenation process was as described in [4]. The specimens for uniaxial tensile testing were manufactured in the same way as the hydrided specimens. The extent of deformation was measured using a strain gauge. The plastic deformation varied from 2 to 9%. As noted in [4], the characteristic parameters for XRD profile analysis are the integral peak width (ds), the average coherent domain size (D) and the distortion factor (El). The ds is a global indicator of the microstructural state of the material. D is the size in a given crystallographic direction of a three-dimensional perfect crystal domain and is limited mainly by crystallographic defects in the specimens, e 1 is the image of the distortion in a given direction induced by the defects around the coherent domains. These three parameters are associated with the distribution of crystallographic defects and with their changes when there is a microstructural change or a mechanical state modification. The usual mean square strain, (e2), corresponding to the microstrain, may be calculated from (e~) = el~L, where L is the characteristic length of cell columns in a sample and equals 100 [4]. The dislocation density is also measured in both cases. Table I shows the XRD profile analysis results: ds, D, el and the dislocation density (p) as functions of the extent of plastic deformation in the mechanically deformed specimens, and as functions of the hydride volume fraction in the hydrided case. The general tendency is for ds, el and p to increase with the extent of plastic deformation and the hydrogen concentration. Conversely, D decreases. The evolution of these parameters produced by mechanical

Microstructural and crystallographic analysis of hydride reorientation in a zirconium alloy cladding tube

Effect of hydride orientation on tensile properties and crack formation in zirconium alloy cladding tubes

Microscopic stress and crystallographic orientation of hydrides precipitated in Zr-1Nb-0.01Cu cladding tube investigated by high-energy X-ray diffraction and EBSD

Hydride precipitation dependence on α-parent orientation and plastic deformation in zirconium alloys

Threshold stress of hydride reorientation in zirconium alloy nuclear fuel cladding tubes: A theoretical determination

Effect of External Stress on Hydride Reorientation in Zirconium

Stress-induced reorientation of hydrides in Zr-1Nb-0.01Cu cladding tube studied by synchrotron X-ray diffraction and EBSD

Effect of Heating Rate on Hydride Reorientation Behavior of Zirconium Alloy Tubes under Non-Stress Loading

Investigation of δ zirconium hydride morphology in a single crystal using quantitative phase field simulations supported by experiments

Hydride-enhanced strain localization in zirconium alloy: a study by crystal plasticity finite element method

Mechanisms of Hydride Nucleation, Growth, Reorientation, and Embrittlement in Zirconium: A Review

Crystal Structure of Hydride Platelets in Hot Rolled Zircaloy-2, Characterized with Synchrotron X-Ray Diffraction, S/TEM, and EELS

Characterization of local deformation around hydrides in Zircaloy-4 using conventional and high angular resolution electron backscatter diffraction

Phase-field simulations of the effect of temperature and interface for zirconium $δ\mbox{-}$hydrides

In-situ EBSD analysis of hydride phase transformation and its effect on micromechanical behavior in Zircaloy-4 under uniaxial tensile loading

Phase-field simulations of the effect of temperature and interface for zirconium δ -hydrides

Hydride Embrittlement in ZIRCALOY-4 Plate: Part II. Interaction Between the Tensile Stress and the Hydride Morphology

Equivalence in Microstructural Evolution Between Hydriding and Plastic Deformation in Recrystallized Zircaloy-4

Development of an advanced hydride reorientation model for Zircaloy cladding and its experimental validation

Quantifying the effect of hydride microstructure on zirconium alloys embrittlement using image analysis

Exploring the Hydride-Slip Interaction in Zirconium Alloys