Revealing the Double‐Edged Behaviors of Heteroatom Sulfur in Carbonaceous Materials for Balancing K‐Storage Capacity and Stability
Yong Qian,Yang Li,Zheng Yi,Jie Zhou,Zhen Pan,Jie Tian,Yusong Wang,Shanshan Sun,Ning Lin,Yitai Qian
DOI: https://doi.org/10.1002/adfm.202006875
IF: 19
2020-11-20
Advanced Functional Materials
Abstract:<p>Heteroatoms in the carbon matrix are generally considered as active sites to enhance potassium storage capacity, while their adverse effects on ion batteries remain unclear. Herein, a series of sulfur doped carbon (SCDP<i>x</i>) with adjustable S content and crystallinity are accurately synthesized in the closed autoclave by controlling the ratios of precursors. Electrochemical measurements exhibit that heteroatom sulfur displays double‐edged electrochemical activities with a high initial potassium storage capacity but poor cycling stability for carbon anode. Combined with solid‐state nuclear magnetic resonance (NMR), catalytic tests, and various ex‐situ characterizations, it is demonstrated that abundant S in the carbon would not only form C<span class="icomoon"></span>S<span class="icomoon"></span>C bonds, acting as active sites to reversibly adsorb/desorb potassium ions for high capacity, but also significantly catalyze the reduction and decomposition of the electrolyte including KPF<sub>6</sub> and ethylene carbonate/diethyl carbonate (EC/DEC) to form thicker solid electrolyte interface (SEI) and degrade electrolyte, resulting in rapid capacity decay. As a result, the optimized sample (SCDP2) with the appropriate sulfur doping content exhibits the best electrochemical performance with high capacity (688.4 mA h g<sup>−1</sup> at 100 mA g<sup>−1</sup>), long‐term cycling stability (198.4 mA h g<sup>−1</sup> at 2000 mA g<sup>−1</sup> after 10 000 cycles), and excellent rate capability (238.8 mA h g<sup>−1</sup> at 5000 mA g<sup>−1</sup>).</p>
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology