Embedding Fe2P nanocrystals in bayberry-like N, P-enriched carbon nanospheres as excellent oxygen reduction electrocatalyst for zinc-air battery

Ruixiang Wang,Yuanliang Yuan,Jianbo Zhang,Xiaocong Zhong,Jiaming Liu,Yongmin Xie,Shuiping Zhong,Zhifeng Xu

DOI: https://doi.org/10.1016/j.jpowsour.2021.230006

IF: 9.2

2021-07-01

Journal of Power Sources

Abstract:<p>Transition metal phosphide/carbon composites are promising electrocatalysts for oxygen reduction reaction (ORR). Herein, we propose a facile process to fabricate a bayberry-like N, P-enriched carbon nanospheres embedded with Fe₂P nanocrystals (Fe₂P/NPCs). Bayberry-like polyaniline nanospheres (PANI-NS) are firstly synthesized through microemulsion template method. Then, Fe is incorporated in PANI-NS during the hydrothermal treatment. Lastly Fe_<em>x</em>P nanocrystals and N, P-enriched carbonaceous carriers are obtained by pyrolyzing the hydrothermal-treated PANI-NS. The resultant Fe_<em>x</em>P/NPCs exhibit a uniform particle size (~250 nm), a large specific surface area (523 m² g⁻¹) and a homogeneous mesoporous structure (~3.46 nm). The phase structure of Fe_<em>x</em>P depends on the Fe/P (molar ratio) during hydrothermal treatment. When Fe/P is around 0.2, a preferable Fe₂P phase is obtained. The Fe₂P/NPCs exhibit outstanding ORR electrocatalytic activity with a half-wave potential of 0.820 V (vs. RHE) and a diffusion-limited current density of 5.58 mA cm⁻², comparable with commercial Pt/C. Moreover, Fe₂P/NPCs possess a good duration stability and higher methanol tolerance than commercial Pt/C. When assembled in zinc-air batteries, Fe₂P/NPCs contribute to an open circuit voltage of 1.449 V, a maximum power density of 128.38 mW cm⁻², and a specific capacity of 691.0 mAh g⁻¹, superior to the commercial Pt/C-based zinc-air battery.</p>

energy & fuels,materials science, multidisciplinary,electrochemistry,chemistry, physical