Abstract:The application of high-strength steels in marine engineering is gaining importance because of their high performance and ability to help save resources. However, detailed and systematic information about the corrosion behavior of high-strength steels in different marine corrosion zones is still limited. This study aimed to investigate and compare the corrosion behavior of AISI 4135 high-strength steel in marine atmospheric, splash, tidal, and immersion zones, focusing on rust layer characteristics, corrosion form and electrochemical corrosion behavior. Corrosion exposure experiments were performed in a specific sea area, and the recovered steel samples were characterized by Raman spectroscopy, confocal laser scanning microscopy, nitrogen adsorption analysis, etc. Results showed that the rust layer formed on the surface of the steel in all corrosion zones had component delamination. The steel samples in the atmospheric, splash, and tidal zones were characterized by pitting corrosion, where the average depths of the corrosion pits were 56.1 ± 4.7 μm, 199.5 ± 12.6 μm, 108.1 ± 11.0 μm, respectively, whereas those in the immersion zone were characterized by general corrosion. Meanwhile, electrochemical tests were performed on the electrode samples during exposure. Results showed that the corrosion of the steel progressed from slow to fast in the atmospheric, splash, and tidal zones, whereas it was relatively steady in the immersion zone. Differentiated models of the corrosion evolution of steel under wet-dry cycle and immersion conditions were presented. This discrepancy is related to the varying degrees of accumulation of ionic corrosion products at the metal/oxide interface, which are determined by the mean pore access diameter of the rust layer and the corrosion environment. This study is highly significant for the design of marine engineering considering the safety applications of high-strength steel structures in harsh marine environments.

Mechanical performance of high strength steel under corrosion: A review study

State-of-the-art Review on the Bond Properties of Corroded Reinforcing Steel Bar

Corrosion Behaviors and Mechanical Properties of Q235 Steel Pipes Collapsing Due to Corrosion after 25-Year Service in Urban Industrial Atmospheric Environment

Mechanical Performance of Artificially Rusted Q500MC Structural Steel Subjected to High Temperature

High-Temperature Mechanical Properties of Artificially Simulated Corroded Q500MC Structural Steel

Mechanical Performance of Corroded Steel Bars in Concrete

Corrosion Behavior of AISI 316L Stainless Steel in a Highly Sour Environment

Corrosion-induced mechanical properties of shear bolted connections in high-strength weathering steel

The effect of acidification on hydrogen uptake and corrosion resistance of advanced high-strength steels

Corrosion Behavior of High Strength Steel Welded Joint in Seawater: A Combinatorial Study Based on General and Localized Electrochemical Methods

Corrosion Resistance of High Performance Weathering Steel for Bridge Building Applications

A review of research on high-strength steel structures

Corrosion-Mechanical Properties and Susceptibility to Hydrogenetaion of Pipe Steel in the Presence of Carbon Dioxide Gas and Hydrogen Sulphide in Environment

Deterioration of Mechanical Properties and the Damage Constitutive Model of Corroded Steel in an Industrial Environment

Evaluation of Hydrogen Permeation into High-Strength Steel during Corrosion in Different Marine Corrosion Zones

Study on corrosion performance and corrosion product composition of weathering steel and high‐performance steel in simulated C3 environment

Effects of Environmental Factors on Corrosion Behavior of E690 Steel in Simulated Marine Environment

Interaction of erosion and corrosion on high-strength steels used for marine dredging engineering

Effects of Alloying Elements and Microstructure on Stainless Steel Corrosion: A Review

Study on corrosion behavior and mechanism of AISI 4135 steel in marine environments based on field exposure experiment

Corrosion of Eutectic High-Entropy Alloys: A Review