Structural and magnetic characterizations of Co2FeGa/SiO2 nanoparticles prepared via chemical route

Priyanka,Rajendra S. Dhaka

DOI: https://doi.org/10.1063/1.5028755

2018-01-01

AIP Conference Proceedings

Abstract:We report the synthesis of Co2FeGa/SiO2 nanoparticles by sol-gel method and characterization usingx-ray diffraction (XRD), transmission electron microscopy (TEM) and magnetic measurements. The Rietveld refinementsof XRD data with space group Fm-3m clearly show the formation of A2 disordersingle phase and the lattice constant isfound to be 5.738 Å. The energy-dispersive x-ray spectroscopy (EDX) confirm the elemental composition close the desired values. The value of coercivity is found to be around 283 Oe and 126 Oe, measured at 10 K and 300 K, respectively. We observed the saturation magnetization significantly lower than expected from Slater-Pauling rule. This decrease in the magnetic moment might be due to the presence of amorphous SiO2 during the synthesis process. A large content of small size SiO2 particles along with Co2FeGa nanoparticles are also found in TEM study.

English Else